在MMS-200热模拟试验机上,采用不同道次压缩法研究了00Cr22Ni5Mo3N双相不锈钢的高温热变形行为,从双道次压缩试验数据中得到不同温度条件下的软化率曲线,并对变形显微组织进行了分析。结果表明：在1~400 s道次间隔时间内,软化率随时间延长而增加,在100 s之内基本完成静态软化。变形温度越高,静态软化行为越明显,在950℃以下时,静态软化不明显;结合试验数据,求出00Cr22Ni5Mo3N双相不锈钢的静态再结晶激活能Qrex=329 kJ/mol;在总变形量0.9,变形温度1 000℃的条件下,相对于2,3道次变形,单道次变形后组织中奥氏体含量要少。随着道次间隔时间的增加,奥氏体组织逐渐细化,相界曲线也由尖锐变得圆滑。
The static softening behavior of 00Cr22Ni5Mo3N duplex stainless steel after hot deformation was investigated by using different-pass compression test in MMS-200 thermo-mechanical simulator.The static softening rate curves at different temperature were concluded based on double-pass compression experimental data,and deformation microstructures were analyzed.The results show that the static softening rate increases as the interval time prolongs in 400s,and the static softening is nearly completed in 100s.The higher the deformation temperature is,the higher the static softening rate is.The static softening behavior is not obvious below 950℃.According to experimental data,the value of 00Cr22Ni5Mo3N duplex stainless steel static recrystallization activation energy（Qrex=329kJ/mol） is gotten.Compared with two or three pass hot deformation,Austenite content is reduced at single pass deformation in the condition of total stain of 0.9 and deformation temperature of 1000℃.Fine austenite microstructures were obtained with increase of interval time,and the phase interface curves were changed from sharp to smooth.
参考文献
| [1] | Siegmund T.;Fischer FD.;Werner E. .ON THE THERMOMECHANICAL DEFORMATION BEHAVIOR OF DUPLEX-TYPE MATERIALS[J].Journal of the Mechanics and Physics of Solids,1995(4):495-532. |
| [2] | L. DUPREZ;B.C. De COOMAN;N. AKDUT .Flow Stress and Ductility of Duplex Stainless Steel during High-Temperature Torsion Deformation[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,2002(7):1931-1938. |
| [3] | A.Iza-Mendia .Microstructural and Mechanical Behavior of a Duplex Stainless Steel under Hot Working Conditions[J].Metallurgical and Materials Transactions, A. Physical Metallurgy and Materials Science,1998(12):2975-2986. |
| [4] | 方轶琉,程逸明,王月香,刘振宇.双相不锈钢热变形行为研究[J].东北大学学报（自然科学版）,2009(08):1124-1126. |
| [5] | 宋红梅,江来珠,余敏,林勤.双相不锈钢2205的热加工性能研究[J].钢铁研究学报,2010(02):41-45,62. |
| [6] | Ying Han;Dening Zou;Zhiyu Chen .Investigation on hot deformation behavior of 00Cr23Ni4N duplex stainless steel under medium-high strain rates[J].Materials Characterization,2011(2):198-203. |
| [7] | 陈雷,王龙妹,杜晓建,刘晓.2205双相不锈钢的高温变形行为[J].金属学报,2010(01):52-56. |
| [8] | 王月香,刘振宇,王国栋,江来珠,宋红梅.2205双相不锈钢热变形过程中形变诱导相变的探讨[J].轧钢,2009(02):6-9. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%