研究淬火-中温回火和等温淬火两种热处理工艺对65Mn钢表面渗硼层组织和性能的影响。结果表明：经该工艺热处理后，65Mn钢表面渗硼试样呈现出典型的表硬芯韧组织特征，其表面为高硬抗磨的硼化物，芯部为强韧的回火屈氏体或下贝氏体；同时，渗硼层物相由以FeB相为主转变为以Fe2B相为主，虽硬度、耐磨性有所下降但其脆性降低了1～2个等级；此外，等温淬火处理在降低热处理应力、保持表面硬度及耐磨性和改善芯部强韧性等方面均好于淬火一中温回火处理。
Effects of quenching and tempering at medium temperature and isothermal quenching on microstructure and properties of boriding layer of 65Mn steel boronized were investigated. The results show that the boronized 65Mn steel after the heat treatment is characterized by typical hard-surface and toughening-core mierostrueture,whieh consists of high-hardness and wear resistant boride layer of surface and tempered troostite or lower bainte with good combination of strength and toughness in core. Meanwhile, the main phase of boriding layer is transformed from FeB to Fe2 B after the head treatment, which results in the brittleness decrease by 1-2 grade although the hardness and wear resistance are also ligtly reduced. Moreover, the isothermal quenching exhibits positive effects in decreasing heat treatment stress, keeping surface hardness and wear resistance and improving strength and toughness of the core than that by quenching and tempering at medium temperature.
参考文献
| [1] | 孟海波,韩鲁佳,刘向阳,阎巧娟,刘依.秸秆揉切机用刀片断裂失效分析[J].农业机械学报,2004(04):51-54,87. |
| [2] | 王宏宇;赵玉风;袁晓明 等.可再制造的适于秸秆全量还田的大耕深旋耕刀[P].中国专利,201110089602.5,2012-11-06. |
| [3] | 郑泽花,张立文,朱大喜,岳重祥.常用钢淬火表面换热系数耦合相变的反传热分析[J].材料热处理学报,2010(05):143-148. |
| [4] | 衣晓红,樊占国,张景垒,李凤华,奚正平.Ti-6Al-4V钛合金固体渗硼法表面改性[J].材料热处理学报,2010(09):119-123. |
| [5] | 周升,伍婵娟,姜佩璐,韦习成.渗硼层对SUS304不锈钢耦合变形的摩擦行为的影响[J].材料热处理学报,2010(06):122-127. |
| [6] | 苏振国,安健,田旭,陆有,杨永利,孙世杰.稀土粉末渗硼45钢的磨损与腐蚀性能[J].材料热处理学报,2009(06):183-186,190. |
| [7] | Yusuf Kayali;Yilmaz Yalcin .The effects of boro-tempering heat treatment on microstructural properties of ductile iron[J].Materials & design,2011(3):1414-1419. |
| [8] | Manoj Mathew;P.K. Rajendrakumar .Optimization of process parameters of boro-carburized low carbon steel for tensile strength by Taquchi method with grey relational analysis[J].Materials & design,2011(6):3637-3644. |
| [9] | Uslu I;Comert H;Ipek M et al.Evaluation of borides formed on AISI PZO steel[J].Materials & Design,2007,28:55-61. |
| [10] | 段汝浩,董智勇,张辉辰.65Mn钢强韧化处理工艺的试验研究[J].农业机械学报,1998(04):126-130. |
| [11] | LI AM;HU MJ .Microstructure and properties of 65Mn steel after austenite inverse phase transformation by sub-temperature quenching[J].Current Advances in Materials and Processes,2011,194-196:89-94. |
| [12] | 刘永J所 .硼化物层脆性的分析与控制[J].机械工程学报,1996,32(01):50-55. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%