通过向Sn-3.5Ag共晶合金中添加质量分数为0.1%,0.3%的锗元素,研究了锗元素对Sn-3.5Ag合金/铜界面反应的影响.结果表明:对于Sn-3.5Ag合金/铜界面,没加入锗元素时界面反应初生相为扇贝状Cu6Sn5,在热老化过程中此化合物层不断长大,且在Cu6Sn5/铜界面处生成新的Cu3Sn化合物,同时在Cu3Sn/铜界面上出现柯肯达尔空洞;当钎料中添加锗后,界面初生相也为Cu6Sn5化合物,在热老化阶段,Cu6Sn5化合物层厚度增长非常缓慢,且无Cu3Sn化合物生成,整个老化过程中都无柯肯达尔空洞出现.
参考文献
| [1] | 贾红星,刘素芹,黄金亮,张柯柯.电子组装用无铅钎料的研究进展[J].材料开发与应用,2003(05):42-46. |
| [2] | Tao-Chih Chang;Moo-Chin Wang;Min-Hsiung Hon .Growth and morphology of the intermetallic compounds formed at the Sn-9Zn-2.5Ag/Cu interface[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2005(1/2):141-148. |
| [3] | F.Ochoa;J.J.Williams;N.Chawla .Effects of Cooling Rate on the Microstructure and Tensile Behavior of a Sn-3.5wt.%Ag Solder[J].Journal of Electronic Materials,2003(12):1414-1420. |
| [4] | Tu P.L.;Chan Y.C.;Lai J.K.L. .Effect of intermetallic compounds on vibration fatigue of μBGAsolder joint[J].IEEE transactions on advanced packaging,2001(2):197-205. |
| [5] | 王烨,黄继华,张建纲,齐丽华.Sn-3.5Ag-0.5Cu/Cu界面的显微结构[J].中国有色金属学报,2006(03):495-499. |
| [6] | 余春,肖俊彦,陆皓.1.0%Zn,Ni对Sn-3.5Ag/Cu界面反应及化合物生长的影响[J].焊接学报,2008(03):81-83. |
| [7] | F. Gao;T. Takemoto;H. Nishikawa .Effects of Co and Ni addition on reactive diffusion between Sn-3.5Ag solder and Cu during soldering and annealing[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2006(1/2):39-46. |
| [8] | 王丽风,孙凤莲,姜志忠,梁英.电子封装中的无铅Sn-3.8Ag-0.5Cu/Cu界面研究[J].哈尔滨理工大学学报,2005(04):16-18. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%