采用不同喷砂工艺对钛基体进行处理,并经草酸溶液刻蚀得到不同粗糙度的基体表面,然后通过热分解法制备氧化物阳极.研究了基体表面粗糙度与氧化物阳极表面粗糙度的关系,并对氧化物阳极进行析氯电位、电流效率、循环伏安曲线及强化电解寿命等性能测试.结果表明,随着基体表面粗糙度的增大,制得的阳极表面粗糙度增大,其电催化活性略微升高,电解寿命得到大幅度提高.
参考文献
| [1] | Efi Tsolaki;Evan Diamadopoulos.Technologies for ballast water treatment:a review[J].Journal of Chemical Technology & Biotechnology,20101(1):19-32. |
| [2] | Seong-Jong KIM;Seok-Ki JANG.Corrosion characteristics of steel in seawater containing various chloride concentrations generated by electrochemical method[J].中国有色金属学报（英文版）,2009(z1):50-55. |
| [3] | 初立英;许立坤;吴连波;王廷勇;王均涛;陈光章.草酸浸蚀对氧化物阳极形貌及电催化性能的影响[J].金属学报,2005(7):763-768. |
| [4] | Krysa J.;Mraz R.;Rousar I.;Kule L..EFFECT OF COATING THICKNESS AND SURFACE TREATMENT OF TITANIUM ON THE PROPERTIES OF IRO2-TA2O5 ANODES[J].Journal of Applied Electrochemistry,199610(10):999-1005. |
| [5] | J. Krysa;J. Maixner;R. Mraz;I. Rousar.Effect of coating thickness on the properties of IrO_2-Ta_2O_5 anodes[J].Journal of Applied Electrochemistry,19983(3):369-372. |
| [6] | 梁成浩;顾谦农.RuO2/TiO2电极在海水电解防污中的电化学行为[J].腐蚀科学与防护技术,1996(02):125. |
| [7] | 张胜健;杜爱玲;许立坤;辛永磊.海水温度对金属氧化物阳极强化电解失效行为影响[J].稀有金属材料与工程,2013(12):2613-2618. |
| [8] | Dan Shao;Wei Yan;Lu Cao;Xiaoliang Li;Hao Xu.High-performance Ti/Sb-SnO_2/Pb_3O_4 electrodes for chlorine evolution: Preparation and characteristics[J].Journal of hazardous materials,2014Feb.28(Feb.28):238-244. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%