选用双马来酰亚胺（BMI）对环氧树脂进行改性，制得一种高强度环氧-酰亚胺体系的ET粘合剂，并对ET粘合剂进行了一系列性能研究。结果表明：ET粘合剂的拉伸剪切强度最高达28.4 MPa，吸水率小于1%，并具有良好的电学性能和工艺性能。
An epoxy resin was modified by bismaleimide resin, and an ET adhesive of epoxy-imide system with high strength was prepared, then its properties were studied. The results show that the ET adhesive has 28.4 MPa of shear strength, below 1% of water absorption and excellent electrical properties and process performance.
参考文献
| [1] | YU Xin-hai,虞鑫海,徐永芬,赵炯心,傅菊荪,石安科,刘万章.耐高温单组分环氧胶粘剂的研制[J].粘接,2008(12):16-19. |
| [2] | 虞鑫海;陈洪江;吴敏 等.一种高强度无溶剂环氧粘合剂的制备方法[P].中国,101544879B,2012-06-13. |
| [3] | 虞鑫海;陈梅芳 .一种耐高温环氧-亚胺树脂胶粘剂及其制备方法[P].中国,102627932A,2012-08-08. |
| [4] | Dobrzynska, J.A.;Gijs, M.A.M. .Flexible polyimide-based force sensor[J].Sensors and Actuators, A. Physical,2012(1):127-135. |
| [5] | Huang XF;Sheng DR;Cen KF;Zhou H .Low-cost relative humidity sensor based on thermoplastic polyimide-coated fiber Bragg grating[J].Sensors and Actuators, B. Chemical,2007(2):518-524. |
| [6] | 周卫新,曾黎明.环氧树脂增韧研究进展[J].中国胶粘剂,2006(05):50-54. |
| [7] | 费斐 .酚羟基聚酰亚胺改性环氧树脂及其固化动力学研究[D].上海:东华大学,2010. |
| [8] | 毛蒋莉,许梅芳,虞鑫海,刘万章.热塑性聚酰亚胺增韧环氧树脂胶粘剂的研制[J].粘接,2010(08):56-59. |
| [9] | Kimiyoshi Naito;Mutsumi Onta;Yasuo Kogo.The effect of adhesive thickness on tensile and shear strength of polyimide adhesive[J].International Journal of Adhesion & Adhesives,2012:77-85. |
| [10] | Ying Fu;Magnus Willander;Johan Liu .Statistics of electric conductance Through anisotropically conductive adhesive[J].IEEE transactions on components and packaging technologies: A publication of the IEEE Components, Packaging, and Manufacturing Technology Society,2001(2):250-255. |
| [11] | 胡利红 .双马来酰亚胺树脂的增韧改性研究[D].南昌航空大学,2012. |
| [12] | 李恩,虞鑫海,徐永芬,刘万章.含羧基聚酰亚胺改性胶粘剂的制备[J].绝缘材料,2012(03):13-15,21. |
| [13] | 虞鑫海.4,4'-双（4-氨基苯氧基）联苯的合成及其聚酰亚胺薄膜的表面性能研究[J].绝缘材料,2008(02):10-14. |
| [14] | 虞鑫海,高欣,徐永芬,傅菊荪,石安科,赵炯心.4,4'-双（4-氨基苯氧基）二苯硫醚及其聚酰亚胺的合成与性能研究[J].绝缘材料,2008(05):10-14. |
| [15] | 费斐,虞鑫海,徐永芬,赵炯心,傅菊荪.4,4' -二氨基-4"-羟基三苯甲烷型聚酰亚胺薄膜的制备及其表面性能研究[J].绝缘材料,2008(02):22-25. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%