Diffusion couples, Fe-6.8 wt% Al-1.0 wt% Si/Fe and Fe-6.3 wt% Al-0.9 wt% Si/Fe were constructed and separately annealed at 1050°C for 3 h and at 1000°C for 64 h. The concentration profiles of Fe, Al and Si atoms in these couples were measured by electron probe micro-analysis (EPMA), while the diffusion behavior was also simulated by coupling thermodynamic and kinetic properties of Fe-Al-Si system. The simulation results were in good agreement with the measured concentration profiles showing the validity of dynamic parameters of Fe-Al-Si system. Calculation was made for Fe-7 wt% Al-1 wt% Si/Fe diffusion couples at 1000°C with different diffusion time. Silicon uphill was found under the in°uence of aluminum.
参考文献
| [1] | S.C. Baik, S. Kim, Y.S. Jin and O. Kwon: ISIJ Int., 2001, 41, 290.[2 ] L. Li, B.C. De Cooman, P.Wollants, Y.L. He and X.D. Zhou: J. Mater. Sci. Technol., 2004, 20, 135.[3 ] W.Y. Lu, L. Li, L. Wang, Y.L. He and S.G. Huang: J. Mater. Sci. Technol., 2008, 24, 771. [4 ] A. Borgenstam, A. Engstrom, L. Hoglund and J. Agren: J. Phase Equilib., 2000, 21, 269.[5 ] J. Wang, H.S. Liu, L.B. Liu and Z.P. Jin: Calphad, 2008, 32, 94.[6 ] G. Ghosh and G.B. Olson: Acta Mater., 2002, 50, 2099.[7 ] Y.L. He, L. Li, S.G. Huang, J. Vleugels and O. Van der Biest: J. Alloy. Compd., 2007, 436, 146.[8 ] J.O. Anderson and J. Agren: J. Appl. Phys., 1992, 72, 1350.[9 ] B. Jonsson: Z. Metallkd., 1994, 85, 502.[10] T. Helander and J. Agren: Acta Mater., 1999, 47, 1141.[11] Y.L. He, L. Li, S.G. Huang, J. Vleugels and O. Van der Biest: Rare Metals, 2007, 26, 492.[12] A. Borgenstam, A. Engstrom, L. Hoglund and J. Agren: J. Phase Equilib., 2000, 21, 269.[13] J.O. Anderson, T. Helander, L. Hoglund, P.F. Shi and B. Sundman: Calphad, 2002, 26, 273.[14] G.M. Hood: Philos. Mag., 1970, 21, 305.[15] S. Fujikawa, K. Hirano and Y. Fukushima: Metall. Trans. A, 1978, 9, 1811.[16] D. Bergner, Y. Khaddour and S. Lorx: Defect Diffusion Forum, 1989, 66-69, 1407.[17] J. Agren: Acta Metall., 1982, 30, 841. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%