用射频磁控溅射方法在硅片上制备了Zn0.93Fe0.07O薄膜,并在空气中用不同温度进行热处理,利用X射线衍射仪和扫描电子显微镜对其微结构、表面和断面形貌进行测试.结果表明,薄膜沿c轴方向择优生长,呈六角纤锌矿结构,空气中450℃退火的样品XRD谱中出现最强的(002)衍射峰,晶粒尺寸变大,薄膜结晶和取向明显变好.用振动样品强磁计对样品铁磁特性进行测试,发现当退火温度的升高时,饱和磁化强度有所增加,并经分析认为这可能是薄膜中晶粒间的晶界缺陷引起的.

参考文献

[1] Han SJ.;Song JW.;Yang CH.;Park SH.;Park JH.;Jeong YH.;Rhie KW..A key to room-temperature ferromagnetism in Fe-doped ZnO: Cu[J].Applied physics letters,200222(22):4212-4214.
[2] Karmakar D;Mandal SK;Kadam RM;Paulose PL;Rajarajan AK;Nath TK;Das AK;Dasgupta I;Das GP.Ferromagnetism in Fe-doped ZnO nanocrystals: Experiment and theory[J].Physical review, B. Condensed matter and materials physics,200714(14):4404-1-4404-14-0.
[3] Yan Lin;Dongmei Jiang;Fan Lin.Fe-doped ZnO magnetic semiconductor by mechanical alloying[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,20071/2(1/2):30-33.
[4] K. Potzger;K. Kuepper;Q. Xu;S. Zhou;H. Schmidt;M. Helm;J. Fassbender.High cluster formation tendency in Co implanted ZnO[J].Journal of Applied Physics,20082(2):023510-1-023510-5-0.
[5] Cebulla R.;Ellmer K.;Wendt R..Al-doped zinc oxide films deposited by simultaneous rf and dc excitation of a magnetron plasma: Relationships between plasma parameters and structural and electrical film properties[J].Journal of Applied Physics,19982(2):1087-1095.
[6] Yamada T;Miyake A;Kishimoto S;Makino H;Yamamoto N;Yamamoto T.Effects of substrate temperature on crystallinity and electrical properties of Ga-doped ZnO films prepared on glass substrate by ion-plating method using DC arc discharge[J].Surface & Coatings Technology,20074/7(4/7):973-976.
[7] 方泽波;龚恒翔;刘雪芹;徐大印;黄春明;王印月.退火对多晶ZnO薄膜结构与发光特性的影响[J].物理学报,2003(7):1748-1751.
[8] 李雪勇;崔丽玲;严钦云.退火温度对Al掺杂ZnO薄膜结构和性能的影响[J].湖南工业大学学报,2011(5):22-25,28.
[9] 叶日晴;赵建华;何陵辉.退火过程中晶粒生长的二维计算机模拟[J].无机材料学报,2001(1):122-128.
[10] 温战华;王立;方文卿;蒲勇;罗小平;郑畅达;戴江南;江风益.退火温度对ZnO薄膜结构和发光性能的影响[J].半导体学报,2005(3):498-501.
上一张 下一张
上一张 下一张
计量
  • 下载量()
  • 访问量()
文章评分
  • 您的评分:
  • 1
    0%
  • 2
    0%
  • 3
    0%
  • 4
    0%
  • 5
    0%