采用液相沉积法对纳米氧化锌进行表面包覆SiO2和SiO2/Al2O3改性,并用XRD、TEM、TG-DSC对其表面结构进行了表征,借助Zeta电位测定仪、静态沉降实验等分析手段考察了改性前后纳米氧化锌在水体系中的分散稳定性.结果表明,在ZnO表面形成的包覆物是以非晶态形式存在的,通过表面包覆SiO2和SiO2/Al2O3改性后明显提高了氧化锌的表面羟基含量,有效改变了氧化锌的等电点,显著提高了纳米氧化锌在水中的分散稳定性.
参考文献
| [1] | Pal U;García Serrano J;Koshizaki N et al.[J].Materials Science and Engineering B:Solid State Materials for Advanced Technology,2004,113(01):24-29. |
| [2] | Shi Jianzhang;Cao Quanxi;Wei Yunge et al.[J].Materials Science and Engineering B-solid State Materials For Advanced Technology,2003,99(1-3):344-347. |
| [3] | Mitra A.;Ganesan V.;Gupta A.;Sahoo PK.;Kulkarni VN.;Thareja RK. .Synthesis and characterization of ZnO thin films for UV laser[J].Applied Surface Science: A Journal Devoted to the Properties of Interfaces in Relation to the Synthesis and Behaviour of Materials,2001(3/4):232-239. |
| [4] | Kobayshi M;Kalriess W .[J].Cosmetics and Toiletries Mag,1997,112:83-86. |
| [5] | 尹春雷,袁方利,黄淑兰.纳米氧化锌表面包覆氧化铝复合粉体制备及其光催化活性[J].过程工程学报,2003(04):346-350. |
| [6] | 沈钟;王果庭.胶体与表面化学[M].北京:北京大学出版社,2001:80-83. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%