对L415/316L复合管进行了充氩和免充氩焊接,采用光学显微镜、电子探针对焊缝组织及主要合金元素分布进行了分析,并采用硬度计测定了接头硬度分布.结果表明,是否采用氩气保护对L415/316L复合管焊接接头组织、化学成分及硬度没有影响.不锈钢层组织为奥氏体和少量铁素体,过渡层为板条状马氏体和类固溶体奥氏体.过渡层焊缝硬度明显高于碳钢层和不锈钢层.背部采用保护剂焊接可以代替传统的充氩焊接,以提高焊接效率.
参考文献
| [1] | M. B. Kermani;A. Morshed .Carbon Dioxide Corrosion in Oil and Gas Production -- A Compendium[J].Corrosion: The Journal of Science and Engineering,2003(8):659-683. |
| [2] | 路民旭,白真权,赵新伟,赵国仙,罗金恒,陈长风.油气采集储运中的腐蚀现状及典型案例[J].腐蚀与防护,2002(03):105-113. |
| [3] | F. M. Song .A comprehensive model for predicting CO_2 corrosion rate in oil and gas production and transportation systems[J].Electrochimica Acta,2010(3):689-700. |
| [4] | 曾德智,杜清松,谷坛,黄黎明,张智,施太和.双金属复合管防腐技术研究进展[J].油气田地面工程,2008(12):64-65. |
| [5] | Spence M A;Roscoe C V .Bi-metal CRA-lined pipe employed for north sea field development[J].Oil and Gas Journal,1999,97(18):80-88. |
| [6] | Chen W C;Petersen C W .Corrosion performance of welded CRA-lined pipes for flow lines[J].SPE Production Engineering,1992,7(04):375-378. |
| [7] | A. M. Torbati;R. M. Miranda;L. Quintino;S. Williams;D. Yapp .Optimization procedures for GMAW of bimetal pipes[J].Journal of Materials Processing Technology,2011(6):1112-1116. |
| [8] | 齐敬春,王明鹏.碳钢内衬不锈钢复合管材的特性及应用[J].中国建材科技,2005(03):23-25. |
| [9] | 钱乐中.油气输送用耐腐蚀双金属复合管[J].特殊钢,2007(04):42-44. |
| [10] | 吕世雄,王廷,冯吉才.20G/316L双金属复合管弧焊接头组织与性能[J].焊接学报,2009(04):93-96. |
| [11] | 王新.双金属复合管焊接工艺研究与应用[J].电焊机,2011(07):71-73. |
| [12] | 许爱华,院振刚,杨光,张靖,张鲲鹏,朱力挥.双金属复合管的施工焊接技术[J].天然气与石油,2010(06):22-28. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%