以微米级MoSi2粉末为原料,利用放电等离子烧结技术制备致密度达99％的MoSi2陶瓷材料.研究烧结温度对MoSi2陶瓷的致密化、微观结构和力学性能的影响.结果表明:SPS烧结技术制备的MoSi2陶瓷由MoSi2、少量的Mo5Si3和SiO2组成;随着烧结温度的升高,材料的致密化效果明显加强;当烧结温度为1600℃时,材料的综合性能最优,相对密度和抗弯强度达到98.9％和417 MPa.但当烧结温度达到1800℃时,致密度基本保持不变,MoSi2晶粒长大明显,材料抗弯强度降低.
参考文献
| [1] | 张来启;高强;林均品.MoSi2超高温结构材料的研究进展[J].中国材料进展,2015(2):126-135. |
| [2] | 韩超 .MoSi2基耐高温涂层的制备及性能研究[D].哈尔滨工业大学,2014. |
| [3] | YAN Jianhui;XU Hongmei;ZHANG Houan;TANG Siwen.MoSi2 oxidation resistance coatings for Mo5Si3/MoSi2 composites[J].稀有金属（英文版）,2009(04):418-422. |
| [4] | Kuchino J;Kurokawa K;Shibayama T;Takahashi H.Effect of microstructure on oxidation resistance of MoSi2 fabricated by spark plasma sintering[J].Vacuum: Technology Applications & Ion Physics: The International Journal & Abstracting Service for Vacuum Science & Technology,20043/4(3/4):623-628. |
| [5] | Shahrouz Zamani;Hamid Reza Bakhsheshi-Rad;Ali Shokuhfar.Synthesis and characterization of MoSi_2-Mo_5Si_3 nanocomposite by mechanical alloying and heat treatment[J].International Journal of Refractory Metals & Hard Materials,2012Mar.(Mar.):236-241. |
| [6] | Wen-Wen Wu;Zhuo Wang;Guo-Jun Zhang.ZrB_2-MoSi2 composites toughened by elongated ZrB_2 grains via reactive hot pressing[J].Scripta materialia,20093(3):316-319. |
| [7] | 王平;熊翔;闵小兵;谢路;王跃明;朱元昌.热喷涂制备MoSi2高温结构材料的工艺研究[J].矿冶工程,2013(2):108-111. |
| [8] | Z. A. Munir.The effect of external electric fields on the nature and properties of materials synthesized by self-propagating combustion[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,20002(2):125-137. |
| [9] | 倪东惠;谭文昌;郑军君;罗汇果;李元元.Si含量对放电等离子烧结制备（1-x）Ti3SiC2+xSiC复合材料的影响[J].中国有色金属学报,2011(6):1279-1284. |
| [10] | 黄平军;张玉勤;蒋业华;周荣.放电等离子烧结温度对Ti-3Zr-2Sn-3Mo-15Nb合金微观组织和力学性能的影响[J].中国有色金属学报,2013(8):2200-2205. |
| [11] | 白玲;葛昌纯;沈卫平.放电等离子烧结技术[J].粉末冶金技术,2007(3):217-223. |
| [12] | 钟群鹏;赵子华;张峥.断口学的发展及微观断裂机理研究[J].机械强度,2005(3):358-370. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%