以SnCl4·5H2O和SbCl3为主要原料,采用共沉淀法制备ATO纳米粉末,用DSC-TG、XRD、FESEM、反射率测试等方法对制得的ATO粉末的形貌、微观结构和激光吸收性能等进行表征.研究结果表明:324℃附近有一个结晶放热峰,说明样品开始发生晶化;XRD分析表明ATO为SnO2四方金红石结构,煅烧温度提高到800℃以后,结晶趋于完善;合成的ATO粉末为不规则球形,初始粒径约为30nm;由于锑的掺杂引起的非化学计量缺陷产生了大量载流子,产生等离子激元效应,并且随着纳米尺寸的减小,纳米晶比表面积增大,因此造成红外吸收峰宽化.
参考文献
| [1] | 刘小强,杜仕国,闫军,崔海萍,程宏凯.国内纳米ATO导电粉体制备的研究现状[J].表面技术,2005(04):6-8. |
| [2] | Lee SY;Park BO .Structural, electrical and optical characteristics of SnO2 : Sb thin films by ultrasonic spray pyrolysis[J].Thin Solid Films: An International Journal on the Science and Technology of Thin and Thick Films,2006(1/2):154-158. |
| [3] | Kim DW;Kim DS;Kim YG;Kim YC;Oh SG .Preparation of hard agglomerates free and weakly agglomerated antimony doped tin oxide (ATO) nanoparticles by coprecipitation reaction in methanol reaction medium[J].Materials Chemistry and Physics,2006(2/3):452-457. |
| [4] | H.-J. Jeon;M.-K. Jeon;M. Kang .Synthesis and characterization of antimony-doped tin oxide (ATO) with nanometer-sized particles and their conductivities[J].Materials Letters,2005(14/15):1801-1810. |
| [5] | 蔡昭军,施利毅,杭建忠.纳米ATO粉体制备及其悬浮液的分散稳定性[J].材料科学与工程学报,2007(05):755-759. |
| [6] | 宋兴华,於定华,马新胜,汪中进.红外低发射率ATO粉末的制备及其特性研究[J].红外技术,2003(06):49-53. |