为了帮助电镀企业选择适合的三价铬镀铬体系，通过实验探讨了3种已获应用的三价铬镀铬溶液体系(硫酸盐、氯化物和硫酸盐-氯化物)与六价铬镀铬溶液体系在镀铬过程中镀液性能、镀层外观色泽和性能之间的差异。结果表明，3种三价铬镀铬体系的电流效率均高于六价铬镀铬体系，所得铬镀层与镍镀层的结合力均好，但镀层硬度较低。其中，硫酸盐镀铬体系的分散能力和覆盖能力最好，得到合格镀层的电流密度范围最宽，所得铬镀层外观色泽乌亮，其耐蚀性与六价铬镀铬相当，但镀速较慢。硫酸盐-氯化物溶液体系镀速较快，电流效率最高；氯化物溶液体系次之，所得铬镀层外观色泽均白亮，但耐蚀性稍差。
The difference of the bath property as well as the appearance, color, luster and performance of chromium deposit obtained from three types of applied trivalent chromium baths including sulfate, chloride, and sulfate-chloride systems from that prepared from a hexavalent chromium plating bath was discussed to help the electroplating corporations selecting suitable trivalent chromium plating system. The results proved that the cathodic current efficiency of all the trivalent chromium plating systems is higher than that of the hexavalent chromium plating system. The adhesion of trivalent chromium deposits to nickel deposit is good, while the hardness is relative low. The sulfate trivalent chromium plating system features the highest throwing power and covering power, the widest current density range over which an eligible chromium deposit is obtained, but relatively low deposition rate, and produces deposits with glossy black appearance and comparable corrosion resistance to the hexavalent chromium deposit. The sulfate-chloride trivalent chromium plating system has advantages of fast plating rate and highest current efficiency, which are better than the chloride system. The deposits obtained from the sulfate-chloride and chloride systems are white and bright, but has a slightly poor corrosion resistance.
参考文献
| [1] | 胡耀红,刘建平,陈力格,赵国鹏,洪榕.硫酸盐三价铬镀铬工艺[J].电镀与涂饰,2006(01):43-45. |
| [2] | RENZ R P;FORTMAN J J;TAYLOR E J.Effects of bath chemistry, solution hydrodynamics, and electrical mediation on trivalent chromium plating[A].Washington:American Electroplaters and Surface Finishers Society,Inc,2001 |
| [3] | 陈磊,陈文汨,龚竹青,涂抚洲,蒋汉瀛.在三价铬Cl--SO2-4体系中电沉积厚镀层的研究[J].材料保护,1999(06):1-2. |
| [4] | 汪启桥,曾振欧,康振华,胡耀红.三价铬硫酸盐溶液镀硬铬的辅助配位剂研究[J].电镀与涂饰,2009(05):5-8,12. |
| [5] | 郑剑,屠振密,李宁,张景双,杨闯.三价铬电镀装饰铬工艺及特性研究[J].材料保护,2008(01):24-27. |
| [6] | 胡耀红,陈力格,赵国鹏,刘建平,洪榕.三价铬镀铬阳极的研究[J].材料保护,2006(04):26-28,31. |
| [7] | 张景双;石金声;石磊.电镀溶液与镀层性能测试[M].北京:化学工业出版社,2003:9-17. |
| [8] | 屠振密.三价铬电镀机理的研究--铬层不能增厚的原因[J].材料保护,1985(03):14. |
| [9] | Liang, A.;Zhang, J. .Why the decorative chromium coating electrodeposited from trivalent chromium electrolyte containing formic acid is darker[J].Surface & Coatings Technology,2012(17):3614-3618. |
| [10] | 刘小珍,李昕,许路坤,王刚.硫酸盐体系三价铬镀铬工艺及镀层性能的研究[J].电镀与环保,2009(06):19-22. |
| [11] | 张新;李惠东;段淑贞 等.三价铬盐镀液电镀硬铬镀层的性能[J].北京科技大学学报,1996,18(01):59-62. |
| [12] | 刘存锟.硫酸盐三价铬电镀新体系的研究[J].化学工业与工程技术,2012(04):8-12. |
| [13] | 张立茗,陈蔡喜.氯化物与硫酸盐三价铬镀铬工艺性能比较[C].2008中国电镀技术研讨会论文集,2008:37-41. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%