采用熔盐电解法,将掺杂CaCO3的TiO2烧结体(作为阴极),在900℃熔盐CaCl2中还原成金属钛.借助SEM,EDS及XRD分析了烧结后的阴极形貌、成分及相组成,考察CaCO3对电解提取钛反应的影响.结果表明:在TiO2阴极中掺杂CaCO3可以增加烧结后的阴极片孔隙度,并影响TiO2颗粒尺寸的大小,有利于加快阴极电解反应的速度,提高电解效率.
参考文献
[1] | Kroll W J .[J].Trans Am Electrochem Soc,1940,78:35. |
[2] | Haarberg G M .[J].Journal of Applied Electrochemistry,1993,23:217. |
[3] | George Chen Z et al.[J].Journal of the Electrochemical Society,2002,149(11):455. |
[4] | Corby Anderson G et al.[J].Rare Metal Materlals and Engineering,2006,35(zk):127. |
[5] | Paillere P.[A].Paris:Soc France Metall,1989:901. |
[6] | Ginatta M V.[A].Paris:Soc France Metall,1989:753. |
[7] | 高敬 et al.[J].金属会刊,2002,38(zk):711. |
[8] | Kuang Oscar Yu .[J].稀有金属材料与工程,2006,35(zk):21. |
[9] | Park Ⅱ et al.[J].J Physics and Chemistry of Solids,2005,66:410. |
[10] | Chen G Z et al.[J].NATURE,2000,407:361. |
[11] | Fray D J et al.[J].Maters Science and Technology,2004,20:295. |
[12] | Katsutoshi Ono .Fundamental Aspects of Calciothermic Process to Produce Titanium[J].Materials transactions,2004(5):1660-1664. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%