The effect of (Ba(0.6)Sr(0.4))TiO3(BST) addition on dielectric properties of CaCu3Ti4O(12) (CCTO) ceramic was investigated. Ceramic samples with the chemical formula (1-x)CaCu3Ti4O(12) + x(Ba(0.6),Sr(0.4))TiO3 (x=0, 0.05, 0.1, and 0.2) were synthesized from high purity oxide powders by the conventional solid-state synthesis method. X-ray diffraction (XRD) analysis showed the existence of BST as a secondary phase alongside CCTO. Scanning electron microscopy (SEM) investigation showed a slight decrease in grain size of doped CCTO samples. Density measurements showed that porosity content increased with increasing BST addition indicating low densification due to high melting point secondary phase addition. Dielectric constant of undoped CCTO (x=0) showed lack of stability with frequency which dropped drastically between 104 and 105Hz and accompanied by high dielectric loss. Addition of BST into CCTO caused the dielectric constant to slightly decrease but improved stability with frequency compared to the undoped sample. The decrease in dielectric constant of doped CCTO samples was suggested to be partly due to the decrease in average grain size and increase in porosity with BST addition. Nevertheless, a high value of dielectric constant was still maintained around ~104 range for all doped samples. The dielectric loss (tanδ) of all BST-doped samples was lower than that of pure CCTO sample at the frequency range of 103 to 105 Hz probably due to the increase of grains boundary resistivity. The activation energy of grains boundary (E(gb)) showed higher values as compared to the activation energy of grains (Eg ) for all samples and conforms to the internal barrier layer capacitor (IBLC) model.
参考文献
| [1] | E. Atanassova;A. Paskaleva .Challenges of Ta_2O_5 as high-k dielectric for nanoscale DRAMs[J].Microelectronics and reliability,2007(6):913-923. |
| [2] | P.B.A.FECHINE;A.TAVORA;L.C.KRETLY .Microstrip Antenna on a High Dielectric Constant Substrate: BaTiO_3 (BTO)-CaCu_3Ti_4O_(12)(CCTO) Composite Screen-Printed Thick Films[J].Journal of Electronic Materials,2006(10):1848-1856. |
| [3] | V. Brize;G. Gruener;J. Wolfman;K. Fatyeyeva;M. Tabellout;M. Gervais;F. Gervais .Grain size effects on the dielectric constant of CaCu_3Ti_4O_(12) ceramics[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2006(1/3):135-138. |
| [4] | W. Si;E. M. Cruz;P. D. Johnson;P. W. Barnes;P. Woodward;A. P. Ramirez .Epitaxial thin films of the giant-dielectric-constant material CaCu_(3)Ti_(4)O_(12) grown by pulsed-laser deposition[J].Applied physics letters,2002(11):2056-2058. |
| [5] | A. F. L. Almeida;P. B. A. Fechine;J. C. Goes .Dielectric properties of BaTiO_3 (BTO)-CaCu_3Ti_4O_(12) (CCTO) composite screen-printed thick films for high dielectric constant devices in the medium frequency (MF) range[J].Materials Science & Engineering, B. Solid-State Materials for Advanced Technology,2004(2/3):113-123. |
| [6] | K.D. Mandal;Alok Kumar Rai;D. Kumar .Dielectric properties of the Ca_(1-x)La_xCu_3Ti_(4-x)Co_xO_(12) system (x = 0.10, 0.20 and 0.30) synthesized by semi-wet route[J].Journal of Alloys and Compounds,2009(1/2):771-776. |
| [7] | J. Li;A.W. Sleight;M.A. Subramanian .Evidence for internal resistive barriers in a crystal of the giant dielectric constant material: CaCu_3Ti_4O_(12)[J].Solid State Communications,2005(4):260-262. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%