以磷酸盐、植酸为主要成分,通过化学沉积的方法在镁合金AZ91D表面获得了无铬磷化膜。经SEM分析表明,膜层存在均匀微裂纹,膜厚为6～10μm;中性盐雾试验,磷化样品72h未见腐蚀现象;电化学极化曲线测试,磷化后镁合金的Ecorr比未处理的正移150mV,Jcorr降低了3个数量级,分析结果进一步证实,磷化膜有效地提高了镁合金AZ91D的耐蚀性能。
A chrome-free phosphate film was prepared on the AZ91D magnesium alloy surface via chemical deposition method.The morphology of surface and interface was examined using scanning electron microscopy（SEM）.The results show that a uniform phosphate film with thickness of 6～10 μm and some micro-cracks can be prepared.The film hardly ethibited corrosion phenomenon for 72 h in the neutral salt spray test（NSS）.The potentiodynamic polarization curves prove that the Ecorr of the alloy with the film was shifted positively by 150 mV（vs.SCE）,the Jcorr was decreased at least by three orders compared with that of the bare substrate.The results confirm that the film possesses good corrosion resistance.
参考文献
| [1] | Guang-Ling Song;ZhenQing Xu .The surface, microstructure and corrosion of magnesium alloy AZ31 sheet[J].Electrochimica Acta,2010(13):4148-4161. |
| [2] | 曾荣昌,兰自栋,陈君,莫鲜花,韩恩厚.镁合金表面化学转化膜的研究进展[J].中国有色金属学报,2009(03):397-404. |
| [3] | 王增辉,卫中领,李春梅,吴森,徐乃欣,陈秋荣.WE43镁合金表面电沉积羟基磷酸钙膜层在模拟体液中的耐腐蚀性[J].腐蚀与防护,2011(03):182-184,189. |
| [4] | 曾荣昌,兰自栋.镀液温度对AZ31镁合金表面锌钙系磷酸盐转化膜耐蚀性的影响[J].中国有色金属学报,2010(08):1461-1466. |
| [5] | 沟引宁,黄伟九,朱翊.AZ91D镁合金表面化学镀Ni-P-SiC复合镀层的结构与性能[J].机械工程材料,2011(03):68-70,75. |
| [6] | 王蕊,马跃洲,陈明,田庆涛.不同电压下镁合金的微弧氧化行为[J].腐蚀与防护,2011(05):363-365,387. |
| [7] | 霍宏伟,李瑛,王福会.化学转化膜上沉积镍对镁合金耐腐蚀性能的影响[J].中国有色金属学报,2004(02):267-272. |
| [8] | Helene Ardelean;Isabelle Frateur;Philippe Marcus .Corrosion protection of magnesium alloys by cerium, zirconium and niobium-based conversion coatings[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2008(7):1907-1918. |
| [9] | 崔秀芳,李庆芬.镁合金表面植酸转化膜研究Ⅰ植酸转化膜成膜机理与耐蚀性研究[J].腐蚀科学与防护技术,2007(03):203-206. |
| [10] | M. F. Montemor;R. Pinto;M. G. S. Ferreira .Chemical composition and corrosion protection of silane films modified with CeO{sub}2 nanoparticles[J].Electrochimica Acta,2009(22):5179-5189. |
| [11] | JIANG Yong-feng,ZHOU Hai-tao,ZENG Su-min.Microstructure and properties of oxalate conversion coating on AZ91D magnesium alloy[J].中国有色金属学报（英文版）,2009(06):1416-1422. |
| [12] | 王章忠,巴志新,戴玉明,夏永平.AZ91D镁合金钼酸盐化学转化表面处理工艺[J].金属热处理,2010(06):93-98. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%