采用激光-氩弧复合焊接技术实现了硬质合金与因瓦合金的焊接,采用扫描电镜、能谱仪以及电子探针等研究了焊缝界面的显微组织、化学成分和元素扩散情况.结果表明:激光和氩弧双热源的作用消除了焊缝界面硬质合金侧的η相,同时在因瓦合金侧形成Fe4WC2枝晶;焊缝硬质合金侧的界面元素扩散系数远高于单独使用氩弧焊焊接条件下的,镍、铁元素的最大扩散系数达到22.7 cm2·s-1,最大扩散距离达到200μm.
参考文献
| [1] | Oh, SH;Kauffmann, Y;Scheu, C;Kaplan, WD;Ruhle, M .Ordered liquid aluminum at the interface with sapphire[J].Science,2005(5748):661-663. |
| [2] | 徐培全,杨德新,赵秀娟,陈春焕,王庆章.Ni-Fe-C对YG30硬质合金与45#钢TIG焊过程中η相形成的影响[J].稀有金属与硬质合金,2003(02):18-23. |
| [3] | Liming Liu;Xinfeng Hao .Improvement of laser keyhole formation with the assistance of arc plasma in the hybrid welding process of magnesium alloy[J].Optics and Lasers in Engineering,2009(11):1242-1249. |
| [4] | C. Barbatti;J. Garcia;G. Liedl;A. Pyzalla .Joining of cemented carbides to steel by laser beam welding[J].Materialwissenschaft und Werkstofftechnik,2007(11):907-914. |
| [5] | A. Costa;L. Quintino;R. M. Miranda .Microstructural aspects of laser dissimilar welds of hard metals to steels[J].Journal of laser applications,2004(4):206-211. |
| [6] | 肖荣诗,吴世凯.激光-电弧复合焊接的研究进展[J].中国激光,2008(11):1680-1685. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%