开展了一系列热处理(500~ 750℃保温30 min后空冷)实验,分析了热处理温度对新型纳米析出强化钢组织性能的影响.结果表明:未热处理钢板的屈服强度和抗拉强度分别为510 MPa和620 MPa,显微组织为铁素体+珠光体;热处理温度在500~660℃之间时,屈服强度上升幅度在20~45 MPa之间;而热处理温度在700 ~750℃之间时,由于形成典型双相钢组织(铁素体+ M/A岛),屈服强度仅为350 MPa.热处理温度在500~660℃之间时发生了(Nb,Ti)C的二次析出,且原有的析出物具有很好的热稳定性,宏观上表现为实验钢屈服强度提高.
参考文献
[1] | 康永林.现代汽车板工艺及成形理论与技术[M].北京:冶金工业出版社,2009:1-12. |
[2] | Misra RDK;Nathani H;Hartmann JE;Siciliano F .Microstructural evolution in a new 770 MPa hot rolled Nb-Ti microalloyed steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):339-352. |
[3] | M. Olasolo;P. Uranga;J.M. Rodriguez-Ibabe;B. López .Effect of austenite microstructure and cooling rate on transformation characteristics in a low carbon Nb–V microalloyed steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2011(6):2559-2569. |
[4] | Kazuhiro S;Yoshimasa F;Shinjiro K .Hot rolled high strength steels for suspension and chassis parts "NANOHITEN" and " BHT (C) steel"[J].JFE Technical Report,2007,10:19-25. |
[5] | Chen, CY;Yen, HW;Kao, FH;Li, WC;Huang, CY;Yang, JR;Wang, SH .Precipitation hardening of high-strength low-alloy steels by nanometer-sized carbides[J].Materials Science and Engineering. A, Structural Materials: Properties, Microstructure and Processing,2009(1/2):162-166. |
[6] | Wang X N;Du L X;Xie H et al.Effect of deformation on continuous cooling phase transformation behaviors of 780MPa Nb-Ti Ultra-high strength steel[J].Steel Research International,2011,82:1417-1428. |
[7] | 王晓南,邸洪双,杜林秀.形变及冷却速率对热轧超高强汽车钢板中纳米析出的影响[J].金属学报,2012(05):621-628. |
[8] | 宋勇军,王晓南,徐兆国,罗继峰,杜林秀.700MPa级超高强重载汽车车厢板的研制[J].机械工程学报,2011(22):69-73,79. |
[9] | Lis J;Lis A K;Kolan C .Processing and properties of C-Mn steel with dual-phase microstructure[J].Journal of Materials Processing Technology,2005,12(05):162-163. |
[10] | Dongsheng LIU;Fateh FAZELI;Matthias MILITZER .Modeling of Microstructure Evolution during Hot Strip Rolling of Dual Phase Steels[J].ISIJ International,2007(12):1789-1798. |
[11] | 雍岐龙.钢铁材料中的析出相[M].北京:冶金工业出版社,2006:145-165. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分:
-
10%
-
20%
-
30%
-
40%
-
50%