热压含碳球团是一种利用煤的热塑性提高冶金性能的新型炼铁原料,具有还原速度快、高温强度高、原料适应性强等优点.在固定碳氧比n(FC)/n(O)为1.00的条件下,通过改变热压含碳球团碱度,系统研究了碱度对热压含碳球团软熔滴落性能的影响.研究表明:碱度对软化区间、熔化区间、滴落率等软熔滴落性能参数有显著的影响.随着碱度的增加,软化区间t40-t4先变窄后加宽,在碱度为1.40时最窄,降至331℃;熔化区间tD-ts先缓慢变窄后急剧加宽,在碱度为1.00时最窄,降至47℃;滴落率先增加后降低,在碱度为1.20时滴落率最高,达到22.22%.从软熔滴落性能角度综合考虑,实际生产热压含碳球团时其适宜的碱度范围为1.00～1.20.
参考文献
| [1] | 付磊,吕继平,柳政根,王兆才,张伟,储满生.铁矿热压含碳球团高温抗压强度的实验研究[C].2008年全国炼铁生产技术会议暨炼铁年会论文集,2008:347-351,357. |
| [2] | Yoshiyuki MATSUI;Muneyoshi SAWAYAMA;Akito KASAI .Reduction Behavior of Carbon Composite Iron Ore Hot Briquette in Shaft Furnace and Scope on Blast Furnace Performance Reinforcement[J].ISIJ International,2003(12):1904-1912. |
| [3] | Kasai A;Matsui Y;Noma F et al.Cold Strength Enhancement Mechanism of Carbon Composite Iron Ore Hot Briquette[J].Tetsu To Hagane-Journal of the Iron & Steel Institute of Japan,2001,87(04):313. |
| [4] | Kasai A;Mataui Y;Miyagawa K.Development of Carbon Composite Iron Ore Hot Briquette and Basic Investigation on Its Strength Enhancing Mechanism and Reducibility[A].Tokyo:MEXT,2003:205. |
| [5] | 储满生,王兆才,艾名星,柳政根.热压含碳球团冷态强度的实验研究[J].东北大学学报（自然科学版）,2009(05):696-700. |
| [6] | 王筱留.钢铁冶金学(炼铁部分)[M].北京:冶金工业出版社,2000 |
| [7] | 杨兆祥.用X-射线透视法研究铁矿石在高温下的软熔过程[J].烧结球团,1985(03):1. |
| [8] | 周取定;孔令坛.铁矿石造块理论与工艺[M].北京:中国金属学会炼铁学术委员会,1985 |
| [9] | 万谷志郎;李宏.钢铁冶炼[M].北京:冶金工业出版社,2001 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%