用旋转水中熔融金属纺丝法制备了Fe-Si-B非晶金属丝。拉伸和弯折性能表明,当合金中杂质碳原子分数含量≥0.2%时,制备态(淬态)非晶丝发生脆化。电子探针、Auger能谱分析与透射电镜观察发现,非晶丝表面具有大约150-300nm宽的富碳层且包含Fe_(23)(C,B)_6相。该相是Fe-Si-B非晶丝脆化的原因。
Fe-Si-B amorphous alloy wires were prepared by the melt spinning in rotating water and the tensile and bending properties of as-cast wires were maesured. Minor carbon, makes the wires embrittle. The enrichment of carbon and the precipatation Fe_(23) (C,B),_6 phases in the surface layer of wires were observed by SEM, TEM and SAM.It seems that Fe_(23) (C, B)_6 induced the embrittlement of as-cast amorphous wires.