采用低熔点Sn-32%Pb-52%Bi合金模拟钢液,研究交变磁场作用下金属熔池液面的波动和变形行为.结果表明:交变磁场会使金属液面发生弧形变形,液面一直处于波动状态;熔池在三相点附近形成汇聚撞击的两个回流区,导致液面上三相点附近的波动最剧烈,易造成表面卷渣;增加线圈电流强度,液面变形增大,波动加剧;当熔池外壁面的磁感应强度达到约50 mT时,液面的波动幅度达到约±3 mm,应有一个合理的电流强度;适当增加频率可减小电磁力对自由表面波动的影响范围,有利于增大弯月面变形和减小液面波动,频率控制在30 kHz左右较适宜;液面位于线圈中心高度附近时,弯月面变形较大,液面波动较剧烈,初始液面控制在线圈高度中心有利于节能.波动规律可解释电磁软接触连铸中铸坯表面振痕随电流强度大小的变化规律.
参考文献
| [1] | VIVES C .Electromagnetic refining of aluminum alloys by the CREM process:Part I.Working principle and metallurgical results[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1989,20(10):623-629. |
| [2] | ZHU X R;HARDING R A;CAMPBELL J .Calculation of the free surface shape in the electromagnetic processing of liquid metals[J].Applied Mathematical Modelling,1997,21:207-214. |
| [3] | 曾德鸿,毛斌,鄂学全.冷坩埚电磁连铸弯月面形状的数值模拟[J].金属学报,2000(02):162-166. |
| [4] | 张斌,李廷举,贾非,季首华.交流电磁场作用下液体金属液面稳定性的研究[J].铸造技术,2002(06):388-389. |
| [5] | 那贤昭,张兴中,仇圣桃,干勇.软接触电磁连铸技术分析[J].金属学报,2002(01):105-108. |
| [6] | 夏小江,王宏明,戴起勋,李桂荣,赵玉涛.电磁软接触连铸高频磁场的数值模拟[J].中国有色金属学报,2008(03):529-534. |
| [7] | HE J C;WANG E G;DENG A Y;YU G W,WANG Q,ZHANG Y J,CHEN Z P,ZHOU Y M,FENG C B.Experiment of soft-contact electromagnetic continuous casting of steel[A].Lylons:EPM Madylam,2003:195-199. |
| [8] | H. NAKATA;T. INOUE;H. MORI .Improvement of Billet Surface Quality by Ultra-high-frequency Electromagnetic Casting[J].ISIJ International,2002(3):264-272. |
| [9] | Joonpyo PARK;Hoyoung KIM;Heetae JEONG .Continuous Casting of Steel Billet with High Frequency Electromagnetic Field[J].ISIJ International,2003(6):813-819. |
| [10] | Yves FAUTRELLE;Damien PERRIER;Jacqueline ETAY .Free Surface Controlled by Magnetic Fields[J].ISIJ International,2003(6):801-806. |
| [11] | KARCHER C;MINCHENYA V.Control of free-surface instabilities during electromagnetic shaping of liquid metals[A].Hannover:University of Hannover,2008:143-149. |
| [12] | 王宏明,任忠鸣,李桂荣.软接触电磁连铸高频磁场的瞬态分析[J].中国有色金属学报,2009(04):701-707. |
| [13] | 张海霞,梁建国,何庆文,韩永刚.液面自控在合金钢连铸机上的应用[J].莱钢科技,2007(04):26-27. |
| [14] | 王文学,王雨,迟景灏.不锈钢连铸坯表面缺陷与对策[J].钢铁钒钛,2006(03):63-68. |
| [15] | 许秀杰,邓安元,王恩刚,张林涛,张兴武,张永杰,赫冀成.电磁软接触连铸圆坯表面振痕演变机理[J].金属学报,2009(04):464-469. |
| [16] | A.Y.Deng,G.L.Jia,J.C.He.THREE-DIMENSIONAL CHARACTERISTICS AND HOMOGENIZATION OF ELECTROMAGNETIC FIELD IN SOFT-CONTACT CONTINUOUS CASTING MOLD[J].金属学报(英文版),2001(02):137-142. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%