A rapidly solidified microcrystalline Al-Li-Cu-Mg-Zr alloy and its superplasicity have been investigated.An optimum tensile elongation of 585% was obtained at 540℃ and strain rate 1.67×10~(-2)s~(-1).The superplastic Al-Li alloy is manufaetured using thermomechanical pro- cessing:solution,overaging,warm rolling and recrystallization.Microstructural changes in thermomechanical processing and cavitation occurred during superplastic deformation have been observed.The superplastic failure of alloy may be caused mainly by nucleation and growth of cavities as well as the linkage around grains.