为了优化金刚石沉积工艺,制备高透射率的CVD金刚石薄膜,采用傅里叶红外光谱仪对不同工艺条件下制备的CVD金刚石膜的红外透射率进行了测量,分析了不同工艺条件对金刚石膜红外透射率的影响,获得了最佳沉积参数.结果表明,金刚石膜的红外透射率与工艺条件密切相关,当衬底温度为750℃,碳源体积分数为2%,压强为2.5 kPa时沉积的金刚石膜红外透射率最佳.
参考文献
| [1] | McCarthy KJ;Lopez JG;Rey DJ;Zurro B;Ibarra A;Baciero A;Respaldiza MA .The response of several luminescent materials to keV and MeV ions[J].Journal of Nuclear Materials: Materials Aspects of Fission and Fusion,2005(2/3):291-298. |
| [2] | C.M.Liddell;C.J.Summers .Nonspherical ZnS colloidal building blocks for three-dimensional photonic crystals[J].Journal of Colloid and Interface Science,2004(1):103-106. |
| [3] | D.W. Zuo;S.L. Song;B.K. Xiang;M. Wang .Some Key Points for EACVD Thick Diamond Film Preparation[J].Key engineering materials,2004(259/260):517-521. |
| [4] | D. Zuo;X. F. Li;M. Wang .Adhesion improvement of CVD diamond film by introducing an electro-deposited interlayer[J].Journal of Materials Processing Technology,2003(1/3):455-457. |
| [5] | 王兵,熊鹰,黎明,李凯.不同反应气源对制备纳米金刚石膜的影响[J].材料科学与工艺,2010(01):96-100. |
| [6] | 孟宪明,王凤英,黑立富,姜春生,唐伟忠,吕反修.沉积参数对化学气相沉积纳米金刚石薄膜的影响[J].材料科学与工艺,2009(03):393-396,401. |
| [7] | 王鸿翔,左敦稳,卢文壮,林欢庆.EACVD小型化系统摆动衬底设计及温度场仿真研究[J].中国机械工程,2009(05):580-584. |
| [8] | 宋贵宏,宫骏,孙超,黄荣芳,闻立时.HFCVD金刚石膜的形貌对红外透射率的影响[J].人工晶体学报,2000(04):390-393. |
| [9] | 施凌云,王林军,蒋丽雯,刘健敏,夏义本.低粗糙度金刚石薄膜的制备及其光学性能的表征[J].上海大学学报（自然科学版）,2007(03):320-324. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%