研究了通过紫外光辐照,在双向拉伸聚丙烯和低密度聚乙烯膜表面制备单分子层羧基的方法.激发态的丙酮分子先从有机聚合物的表面夺取C-H键的氢,生成大分子链自由基;然后过氧化丁二酸(BOS)裂解产生的带羧基的自由基与大分子链自由基偶合形成羧基.通过水接触角(CA)、紫外吸收光谱(UV)、X射线光电子能谱(XPS)和酸碱滴定等试验,证明在聚合物基材表面有羧基.对反应的工艺参数,如光照强度,光照时间、反应液的配方及BOS浓度等进行了考察.最佳的条件为:光强为8500μW/cm2,丙酮/水=3/7,BOS溶液为1%(质量/体积),光照15min.
参考文献
| [1] | Wang YX;Deng JP;Zhong WB;Kong LB;Yang WT .Facile surface superhydrophilic modification: NVP/MBA inverse microemulsion surface-grafting polymerization initiated by UV light[J].Macromolecular rapid communications: Publishing the newsletters of the European Polymer Federation,2005(22):1788-1793. |
| [2] | Xing CM;Deng JP;Yang WT .Synthesis of antibacterial polypropylene film with surface immobilized polyvinylpyrrolidone-iodine complex[J].Journal of Applied Polymer Science,2005(5):2026-2031. |
| [3] | Yang P;Sun YF;Deng JY;Liu WN;Zhang L;Yang WT .Synthesis and inhibition performance of a polymer-supported inhibitor[J].Journal of Polymer Science, Part A. Polymer Chemistry,2004(16):4074-4083. |
| [4] | 胡飞,胡辉,肖静芝.紫外光固化涂料对金属基材附着力的研究[J].电镀与涂饰,1999(02):37-39. |
| [5] | 林贤福,何琳,徐立恒,吕德水,陈志春.脂肪酶在负离子化PET表面的单分子层自组装膜研究[J].高等学校化学学报,2001(04):383-386. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%