以低聚物多元醇、异佛尔酮二异氰酸酯(IPDI)为主要原料,N-甲基二乙醇胺(MDEA)和1,4-丁二醇为扩链剂,采用自乳化法制备端羟基聚丁二烯-丙烯腈(HTBN)改性阳离子聚氨酯树脂；以异佛尔酮二异氰酸酯、N-甲基二乙醇胺、1,4-丁二醇为原料制备封端交联剂,二者混合、分散后进行电泳成膜.探究了HTBN的用量、软段种类、树脂与交联剂的比例以及中和度对漆膜性能的影响,结果表明:使用HTBN和PTMG-1000作为混合软段,HTBN在树脂中的质量分数为7.9％,树脂与交联剂的官能团物质的量比为1∶1.1,树脂中和度为90％时,能较好地改善漆膜性能.
参考文献
| [1] | 莫京辉.电泳涂料的选择[J].现代涂料与涂装,1996(03):39. |
| [2] | 王幸芬 .水性双组分聚氨酯涂料[J].涂料工业,1999,29(04):10-11. |
| [3] | M.ANGELES PEREZ-LIMINANA;FRANCISCA ARAN-AIS;ANA M.TORRO-PALAU;CESAR ORGILES-BARCELO;JOSE MIGUEL MARTIN-MARTINEZ .Structure and properties of waterborne polyurethane adhesives obtained by different methods[J].Journal of Adhesion Science and Technology: The International Journal of Theoredtical and Basic Aspects of Adhesion Science and Its Applications in All Areas of Technology,2006(6):519-536. |
| [4] | MARTIN MELCHIORS;MICHAEL SONNTAAG;CLAUS KOBUSCH et al.Recent evelopments in aqueous two-component polyurethane (2K-PUR.) coatings[J].Progress in Organic Coatings,2000,40(1-4):99-109. |
| [5] | 许戈文.水性聚氨酯材料[M].北京:化学工业出版社,2006 |
| [6] | 李敏婷,李金艳,刘晓丹,董慧民,李再峰.阴极聚氨酯电泳树脂的制备及电泳工艺参数优化[J].涂料工业,2010(10):66-69. |
| [7] | 周荣明,胡和丰,严惠根.紫外光固化阴极电泳涂料涂装过程的探讨[J].上海大学学报(自然科学版),2000(05):448-452. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%