通过草酸共沉淀法成功合成了5 V正极材料LiNi0.5Mn1.5O4,采用XRD、SEM、充放电试验和循环伏安法对合成产物进行表征.XRD和SEM分析结果表明,所合成的正极材料LiNi0.5Mn1.5O4具有立方尖晶石结构(空间群为Fd(3)m),结晶度高,粒度适中且比较均匀.电化学测试结果表明,合成产物具有优良的电化学性能,它仅在4.7V附近有一个放电平台,0.1 C的放电容量高达133 mAb/g,50次循环后放电容量仍保持在128 mAh/g以上,1和3 C的放电容量在30次循环后也分别保持在122和101 mAh/g以上.
5 V cathode material LiNi0.5Mn1.5O4 was synthesized via an oxalate co-precipitation process. The synthesized product was characterized by XRD, SEM, charge/discbarge test and cyclic voltammetry. XRD and SEM results indicate that the synthesized product LiNi0.5Mn1.5O4 has cubic spinel structure with space group of Fd3m, high crystallinity, moderate and uniform particle size.The electrochemical experiment results show that the LiNi0.5Mn1.5O4 has excellent performances. It has only one discharge plateau at around 4.7 V. 0.1 C discharge capacity is up to 133 mAh/g and retains above 128 mAh/g after 50 cycles, 1 C and 3 C discharge capacities after 30 cycles also retain above 122 mAh/g and 101 mAh/g, respectively.
参考文献
| [1] | Atsushi Ito;Decheng Li;Yunsung Lee;Koichi Kobayakawa;Yuichi Sato .Influence Of Co Substitution For Ni And Mn On The Structural And Electrochemical Characteristics Of Lini_(0.5)mn_(1.5)o_4[J].Journal of Power Sources,2008(2):1429-1433. |
| [2] | Locati C;Lafont U;Simonin L .[J].Journal of Power Sources,2007,174(02):847. |
| [3] | Masaki Okada;Yon-Sung Lee;Masaki Yoshio .[J].Journal of Power Sources,2000,90(02):196. |
| [4] | Sang-Ho Park;Yang-Kook Sun .[J].Electrochimica Acta,2004,50(2-3):434. |
| [5] | Lafont U;Locati C;Kelder EM .Nanopowders of spinel-type electrode materials for Li-ion batteries[J].Solid state ionics,2006(35/36):3023-3029. |
| [6] | SUN Qiang,LI Xin-hai,WANG Zhi-xing,JI Yong.Synthesis and electrochemical performance of 5V spinel LiNi0.5Mn1.5O4 prepared by solid-state reaction[J].中国有色金属学会会刊（英文版）,2009(01):176-181. |
| [7] | Chen Zhaoyong;Zhu Huali;Ji Shan et al.[J].Transactions of Nonferrous Metals Society of China,2008,18(01):507. |
| [8] | Lei Wen;Qi Lu;Guoxiang Xu .Molten salt synthesis of spherical LiNi{sub}0.5Mn{sub}1.5O{sub}4 cathode materials[J].Electrochimica Acta,2006(21):4388-4392. |
| [9] | Zhang Lianqi;Yabu Takeo;Taniguchi Izumi .[J].Materials Research Bulletin,2009,44(03):707. |
| [10] | Y. S. Lee;Y. K. Sun;S. Ota;T. Miyashita;M. Yoshio .Preparation and characterization of nano-crystalline LiNi_(0.5)Mn_(1.5)O_4 for 5 V cathode material by composite carbonate process[J].Electrochemistry communications,2002(12):989-994. |
| [11] | Fan Yukai;Wang Jianming;Ye Xuebo et al.[J].Materials Chemistry and Physics,2007,103(01):19. |
| [12] | Fang Haisheng;Wang Zhixing;Zhang Bao .[J].Electrochemistry Communications,2007,9(05):1077. |
| [13] | Yi Tingfeng;Shu Jie;Zhu Yanrong et al.[J].Electrochemistry Communications,2009,11(01):91. |
| [14] | Alca'ntara R;Jaraba M;Lavela P et al.[J].Electrachimica Acta,2002,47(07):1829. |
| [15] | Fang Haisheng;Wang Zhixing;Li Xinhai et al.[J].Materials Letters,2006,60(9-10):1273. |
| [16] | Liu G Q;Wang Y J;Qi Lu et al.[J].Electrochimica Acta,2005,50(09):1965. |
| [17] | Yi Tingfeng;Zhu Yanrong .[J].Electrochimica Acta,2008,53(07):3120. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%