利用扫描电镜和图象分析仪研究了纯铁加稀土元素(La、Ce、Y)或Al脱氧后铁液中氧化物夹杂的形貌、颗粒大小及尺寸分布,并考察了脱氧元素种类、孕育时间和冷却速度对夹杂物尺寸的影响.研究结果表明:铁液脱氧产物为稀土氧化物(或Al2O3)与氧化铁形成的复合型夹杂物.此类夹杂物呈细小弥散分布.适宜的孕育时间和较快的冷却速度可使夹杂物细化.在4种脱氧元素中,La细化夹杂物的效果最好.