采用真空氩弧熔炼加铜模吸铸的方法成功制备了3种ZrAlNiCu全非晶材料.通过Instron-3369力学性能试验机测试了3种金属玻璃的压缩力学性能,并采用FEI Nano230型场发射扫描电镜(SEM)研究了压缩断口特征.研究表明,增加Ni含量和降低Cu含量将降低ZrAlNiCu金属玻璃的断裂强度和弹性模量,并使得ZrAINiCu金属玻璃的断口由扩展良好的“脉络状”花纹转变为完全脆性特征.Ni含量的增加以及Cu含量的降低减少了ZrAlNiCu金属玻璃中自由体积的密度,降低了合金的变形能力,增加了合金的变形局域化程度,从而降低了ZrAlNiCu金属玻璃的断裂强度、塑性和弹性模量.
参考文献
| [1] | Klement W;Willens R H;Duwez P .[J].Nature,1960,187:869. |
| [2] | Inoue A;Zhang T;Ma8umoto T .[J].Materials Transactions-Japan Institute of Metals,1989,30:965. |
| [3] | Inoue A;Zhang T;Masumoto T .[J].Materials Transactions-Japan Institute of Metals,1990,31(03):177. |
| [4] | Peker A;Johnson W L .[J].Applied Physics Letters,1993,63(17):2342. |
| [5] | 孙军,张国君,刘刚.大块非晶合金力学性能研究进展[J].西安交通大学学报,2001(06):640-645. |
| [6] | 孙剑飞,陈德明,沈军,梁立孚,刘殿魁.Zr基大块非晶合金的制备及力学性能[J].固体火箭技术,2002(04):56-58,74. |
| [7] | Wang X Y;Sun L L;Li G et al.[J].Journal of Materials Science Letters,2003,22:171. |
| [8] | 王秀英,孙力玲,刘日平,姚玉书,张君,王文魁.高压下Co在Zr46.755Ti8.25Cu7.5Ni10Be27.5大块金属玻璃过冷液相区中的扩散[J].物理学报,2004(11):3845-3848. |
| [9] | 褚维,陈国钧.大块非晶合金的研究进展[J].磁性材料及器件,1999(01):7-11. |
| [10] | 王秀英,高明,孙力玲,刘日平,张君,王文魁.注入Mo 在Zr57Nb5Cu15.4Ni12.6Al10非晶合金中的扩散[J].物理学报,2004(01):200-203. |
| [11] | Inoue A;Takeuchi A .[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,375-377:16. |
| [12] | Inoue A.;Zhang T.;Kimura HM. .High-strength aluminum- and zirconium-based alloys containing nanoquasicrystalline particles[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2000(0):727-735. |
| [13] | Fátay D;Gubicza J;Szommer P et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,387-389:1001. |
| [14] | Jing Q;Liu R P;Li G et al.[J].Scripta Materialia,2003,49:111. |
| [15] | Ma M Z;Liu R P;Xiao Y et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2004,386:326. |
| [16] | Turnbull D;Cohen M H .[J].Journal of Chemical Physics,1961,34:120. |
| [17] | Turnbull D;Cohen M H .[J].Journal of Chemical Physics,1970,52:3038. |
| [18] | Cohen M H;Turnbull D .[J].Journal of Chemical Physics,1959,31:1164. |
| [19] | Spaepen F .[J].Acta Metallurgica,1977,25:407. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%