利用SEM、EDx和XRD等方法分析了在点焊镀锌钢板时电极表面熔敷TiC涂层对电极失效的影响.结果表明:点焊镀锌钢板时电极的失效机制主要是电极和镀锌板之间局部焊接的断裂发生在电极表面而导致的电极磨损,以及电极和镀锌板表面的锌之间的合金化.表面涂敷TiC的CuCrZr电极的寿命(1 200点)是CuCrZr电极寿命(500点)的2.4倍,表面处理能提高电极寿命的主要原因是在点焊镀锌钢板时表面涂敷的TiC层能阻碍电极和镀锌板之间的局部焊接和阻碍电极和镀锌板表面的锌之间的合金化.
参考文献
| [1] | Holliday R;Parker J D;Williams N T .Electrode deformation when spot welding coated steels[J].Welding in the world,1995,35(03):160-164. |
| [2] | Takahashi Y;Saito T .Electrode tip wear and tip life in resistance spot-welding of organic composite coated steels, study of resistance spot-welding of coated steels (1)[J].Welding International,1994,8(04):262-268. |
| [3] | Chatterjee K L;Waddel[ W.Electrode wear during spot welding of coated steel[J].Welding & Metal Fabrication,1996(03):110-114. |
| [4] | Tanaka Y;Sakaguchi M;Shirasawa H et al.Electrode life in resistance spot welding of zinc plated steel sheets[J].International Journal of Materials and Product Technology,1987,2(02):286-291. |
| [5] | Gedeon S A;Eagar T W .Resistance spot welding of galvanized steel: part Ⅰ. Material variations and process modifications[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1986,17(12):879-885. |
| [6] | Gedeon S A;Eagar T W .Resistance spot welding of galvanized steel: part Ⅱ. Mechanisms of spot weld nugget formation[J].Metallurgical and Materials Transactions B:Process Metallurgy and Materials Processing Science,1986,17(12):887-901. |
| [7] | R. J. Holliday;J. D. Parker;N. T. Williams .Prediction of electrode campaign life when spot welding zinc coated steels incorporating electrode tip dressing operations[J].Ironmaking & Steelmaking: Products and applications,1996(2):157-163. |
| [8] | Holliday R;Parker J D;Williams N T .Relative contribution of electrode tip growth mechanisms in spot welding zinc coated steels[J].Welding in the world,1996,36(04):186-193. |
| [9] | Dong P;Li M V;Kimchi M .Finite element analysis of electrode wear mechanisms: face extrusion and pitting effects[J].Science Technology Industry Review,1998,3(02):59-64. |
| [10] | O'brien R L.Welding Handbook(Vol.2).8th edition[M].Miami:American Welding Society,1991 |
| [11] | Parker J D;Williams N T;Hollidag R J .Mechanisms of electrode degradation when spot welding coated steels[J].Science and Technology of Welding and Joining,1998,3(02):65-74. |
| [12] | DONG S J;Zhou Y .Effect of TiC conposite coating on electrode degradation in microresistance welding on nickel-plated steel[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,2003,34(07):1501-1511. |
| [13] | Holliday R;Parker J D;Williams N T .Relative contribution of electrode tip growth mechanisms in spot welding zinc coated steels[J].Welding in the world,1996,37(04):186-193. |
| [14] | Shackelford J F;Alexander W.Materials Science and Engineering Handbook. 3rd ed[M].Florida:CRC Press LLC,2001 |
| [15] | DONG S J;Kelkar G P;Zhou Y .Electrode sticking during micro-resistance welding of thin metal sheets[J].IEEE transactions on electronics packaging manufacturing,2002,25(04):355-361. |
| [16] | Prabhjit S .Wear Mechanism and Technology Improvement of TiC Cap Electrode for Resistance Spot Welding[D].Waterloo: The University of Waterloo,2002. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%