以Ca(OH)2、SiO2化学纯为原料,分别掺入不同质量分数的Ni2O3制备不同晶型的G3S相,运用化学分析、XRD、DTA、SEM、水化热测试方法,研究了掺Ni2O3后C3S矿物相形成、晶型及其水化特性变化趋势.结果表明,Ni2O3促进C3S形成效应一般,掺量大于2％后促进效应增强；且掺量大于2％时,Ni2O3可稳定单斜型C3S存在；合Ni的G3S具有一定的活性点或活性面,水化后会导致液相呈现较高的Ca2+浓度,轻微地加快了G3S水化速率,且水化产物颗粒较小,分散度和水化程度高.
参考文献
| [1] | Stephan D.;Mallmann R. .High intakes of Cr, Ni, and Zn in clinker Part I. Influence on burning process and formation of phases[J].Cement and Concrete Research,1999(12):1949-1957. |
| [2] | Stephan D;Maleki H;Knofel D et al.Influence of Cr,Ni and Zn on the properties of pure clinker phases:Part Ⅰ.C3S[J].Cement and Concrete Research,1999,29(04):545. |
| [3] | A. Wesselsky;O.M. Jensen .Synthesis of pure Portland cement phases[J].Cement and Concrete Research,2009(11):973-980. |
| [4] | Martínez I M .Synthesis and stability of α-tricalcium phosphate doped with dicalcium silicate in the system Ca3 (PO4)2-Ca2SiO4[J].Cement and Concrete Research,2010,61(07):761. |
| [5] | 迪安JA.兰氏化学手册[M].北京:科学出版社,1991 |
| [6] | 沈威;黄文熙;闵盘荣.水泥工艺学[M].武汉:武汉工业大学出版社,1991:67. |
| [7] | 袁润章.胶凝材料学[M].武汉:武汉工业大学出版社,1996:119. |
| [8] | Huang Baoshan .Laboratory investigation of Portland cement concrete containingrecycled asphalt pavements[J].Cement and Concrete Research,2005,35(12):2008. |
| [9] | Kazuyori Urabe;Hiromi Nakano .Structural modulations in monoclinic tricalcium silicate solid solution doped with zinc oxide M(Ⅰ) M(Ⅱ) M(Ⅲ)[J].Cerarn Soc,2002,85(02):423. |
| [10] | Kazuyori Urabe;Tatsuya Shirakami;Minori Iwashima .Superstructure in a triclinic phase of tricalcium silicate[J].Journal of the American Ceramic Society,2000(5):1253-1258. |
| [11] | 周亚栋.无机材料物理化学[M].武汉:武汉工业大学出版社,1994 |
| [12] | 祁景玉.X射线结构分析[M].上海:同济大学出版社,2003 |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%