采用拉伸性能测试、剥落腐蚀实验及透射电镜观察研究了175℃回归时7150-RRA铝合金力学性能、剥蚀行为及微观组织,并与T6及T73时效工艺进行了比较研究.结果表明,7150-T6铝合金强度高而剥蚀敏感性大;7150-T73铝合金强度降低而耐腐蚀性大幅度提高.175℃回归时,7150-RRA铝合金剥蚀敏感性随回归时间延长而降低;回归时间延长至3h,7150-RRA铝合金可保持7150-T6的高强度,而其剥蚀敏感性与7150-173接近.
参考文献
| [1] | 刘继华,李荻,刘培英,郭宝兰,朱国伟.时效和回归处理对7075铝合金力学及腐蚀性能的影响[J].材料热处理学报,2002(01):50-53. |
| [2] | Xigang Fan;Darning Jiang;Li Zhong .Influence of microstructure on the crack propagation and corrosion resistance of Al-Zn-Mg-Cu alloy 7150[J].Materials Characterization,2007(1):24-28. |
| [3] | 曾渝,尹志民,朱远志,潘青林,周昌荣.RRA处理对超高强铝合金微观组织与性能的影响[J].中国有色金属学报,2004(07):1188-1194. |
| [4] | 谷亦杰,林建国,张永刚,陈昌麒.回归再时效（RRA）处理对7050铝合金的影响[J].金属热处理,2001(01):31-35. |
| [5] | Standard test method for exfoliation corrosion susceptibility in 2XXX and 7XXX series aluminum alloys(EXCO test).ASTM G34-01[R].,2007. |
| [6] | Dixit M;Mishra RS;Sankaran KK .Structure-property correlations in Al 7050 and Al 7055 high-strength aluminum alloys[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2008(1/2):163-172. |
| [7] | 郑子樵,李红英,莫志民.一种7055型铝合金的RRA处理[J].中国有色金属学报,2001(05):771-776. |
| [8] | 谷亦杰,李永霞,张永刚,黄正,陈昌麒.7050合金RRA沉淀析出的TEM研究[J].航空材料学报,2000(04):1-7. |
| [9] | 李杰 .热处理对7055合金组织和性能的影响[D].中南大学,2005. |
| [10] | 李劲风,郑子樵,任文达.第二相在铝合金局部腐蚀中的作用机制[J].材料导报,2005(02):81-83,90. |
| [11] | 李狄;左尚志;郭宝兰 .LY12铝合金剥蚀行为的研究[J].中国腐蚀与防护学报,1995,15(03):203-209. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%