采用静态高压釜设备,研究了经表面喷丸和未喷丸处理的800合金管,在含1 200 mg·L-1硼和2 mg·L-1锂的低溶解氧模拟压水堆(PWR)—回路高温水溶液中的均匀腐蚀行为.结果表明,在3 000 h腐蚀试验后,试样表面金属氧化物部分溶解于水中,剩余部分附着在基体表面形成氧化膜.经过喷丸处理后,800合金管的均匀腐蚀减重速率增加;点腐蚀发生的可能性增大;晶间腐蚀敏感性增强.
参考文献
| [1] | Chen YY;Chou LB;Shih HC .Factors affecting the electrochemical behavior and stress corrosion cracking of Alloy 690 in chloride environments[J].Materials Chemistry and Physics,2006(1):37-49. |
| [2] | 朱小明,黄红波,林俊,夏元复,丁亚平,徐雪莲.用XPS分析喷丸处理后800合金在强碱溶液中的腐蚀产物[J].中国腐蚀与防护学报,2004(04):213-217. |
| [3] | 乔培鹏,张乐福,刘瑞芹,朱发文.PWR一回路水质中800合金的腐蚀研究[J].核动力工程,2010(05):28-31. |
| [4] | Stephen E. Ziemniak;Michael Hanson .Corrosion behavior of NiCrFe Alloy 600 in high temperature, hydrogenated water[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2006(2):498-521. |
| [5] | Azar, V.;Hashemi, B.;Rezaee Yazdi, M. .The effect of shot peening on fatigue and corrosion behavior of 316L stainless steel in Ringer's solution[J].Surface & Coatings Technology,2010(21/22):3546-3551. |
| [6] | 黄春波,吕战鹏,杨武.改性800合金碱性SCC机理研究[J].腐蚀与防护,2003(01):1-5. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%