Electrically Conductive Honeycomb Monolith of Nanolaminated Ti3AlC2: Preparation and Characterization

材料科学技术（英文）, 2015, 31(1): 125-128.

X.M. Fang ^1, , X.H. Wang ^2, , H. Zhang ^3, , Y.C. Zhou ^4,

1.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016,China;University of Chinese Academy of Sciences, Beijing 100049, China

2.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016,China

3.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016,China;University of Chinese Academy of Sciences, Beijing 100049, China

4.Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016,China;Science and Technology of Advanced Functional Composite Laboratory, ARIMPT, Beijing 100076, China

基金项目: This work was supported by the National Natural Science Foundation of China (Nos.50802097 and 50832008),and the Scientific Research Foundation for the Returned Overseas Chinese Scholars,State Education Ministry.

Electrically Conductive Honeycomb Monolith of Nanolaminated Ti3AlC2: Preparation and Characterization

Keywords： Honeycomb ceramic

参考文献

[1]	H. Santos;M. Costa .Evaluation of the conversion efficiency of ceramic and metallic three way catalytic converters[J].Energy conversion & management,2008(2):291-300.
[2]	J. R. Gonzalez-velasco;M. A. Gutierrez-ortiz .Synthesis of cordierite monolithic honeycomb by solid state reaction of precursor oxides[J].Journal of Materials Science,1999(9):1999-2002.
[3]	N.V.Tzenov;M.W.Barsoum .Synthesis and characterization of Ti_3AlC_2[J].Journal of the American Ceramic Society,2000(4):825-832.
[4]	X. H. Wang;Y. C. Zhou .Microstructure and properties of Ti_3AlC_2 prepared by the solid-liquid reaction synthesis and simultaneous in-situ hot pressing process[J].Acta materialia,2002(12):3141-3149.
[5]	Y.W. Bao;X.H. Wang;H.B. Zhang .Thermal shock behavior of Ti_3AlC_2 from between 200 deg C and 1300 deg C[J].Journal of the European Ceramic Society,2005(14):3367-3374.
[6]	X.H. Wang,Y.C. Zhou.Layered Machinable and Electrically Conductive Ti2AlC and Ti3AlC2 Ceramics: a Review[J].材料科学技术学报（英文版）,2010(05):385-416.
[7]	G-P. Bei;G. Laplanehe;V. Gauthier-Brunet .Compressive Behavior of Ti_3AlC_2 and Ti_3Al_(0.8)Sn_(0.2)C_2 MAX Phases at Room Temperature[J].Journal of the American Ceramic Society,2013(2):567-576.

上一张下一张

计量

下载量()
访问量()

作者相关

在本站搜索
X.M. Fang X.H. Wang H. Zhang Y.C. Zhou
在百度学术搜索
X.M. Fang X.H. Wang H. Zhang Y.C. Zhou
在万方数据库搜索
X.M. Fang X.H. Wang H. Zhang Y.C. Zhou
在CNKI搜索
X.M. Fang X.H. Wang H. Zhang Y.C. Zhou

文章评分

您的评分：
1

0%
2

0%
3

0%
4

0%
5

0%

材料期刊网

Electrically Conductive Honeycomb Monolith of Nanolaminated Ti3AlC2: Preparation and Characterization

参考文献