通过模拟退火试验研究了气冷连续退火工艺对冷轧双相钢板组织和力学性能的影响.结果表明,随均热温度升高,钢板强度首先大幅下降,之后逐渐上升到最高点,然后又有所下降,退火温度应保证均热时得到一定数量的奥氏体,但对于喷气冷却的快速冷却工艺,过高温度产生过多的奥氏体降低了淬透性,不利于钢板力学性能;均热后适当的缓冷町以析出新生铁素体,这有利于双相钢板的塑性.
参考文献
| [1] | 马鸣图.汽车结构用钢的进展[J].汽车工程,2005(03):269-273. |
| [2] | 马鸣图;吴宝榕.双相钢-物理和力学冶金[M].北京:冶金工业出版社,1998 |
| [3] | R.O. Rocha;T.M.F. Melo;E.V. Pereloma .Microstructural evolution at the initial stages of continuous annealing of cold rolled dual-phase steel[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2005(1/2):296-304. |
| [4] | 朱晓东,王利,俞宁峰,季思凯,王聪.过时效和平整对冷轧双相钢板强度、塑性及烘烤硬化性的影响[J].钢铁研究学报,2003(06):47-50. |
| [5] | Kubtera H;Nakaoka K.Development of a Continuous Annealing Process for the Drawing Quality Steel Strip[J].Transactions of the Iron and Steel Institute of Japan,1977(17):663. |
| [6] | M Erdogan.The Effect of New Ferrite Content on the Tensile Fracture Behavior of DP Steel[J].Journal of Materials Science,2002(37):3623. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%