采用活化剂（尿素、碳酸锌）和碳酸氢钠对偶氮二甲酰胺（AC）改性制备硬质聚氯乙烯（R-PVC）用复合发泡剂,并用热分析和放气量检测对复合发泡剂进行了表征。结果表明当AC、NaHCO3、尿素和碳酸锌的质量比为10：10：2.5：2.5时所得的复合发泡剂分解温度处于R-PVC成型加工范围内,吸-放热基本平衡,放气量大且无突发性。采用这种复合发泡剂制备的硬质聚氯乙烯发泡材料具有较好的力学性能和微孔结构。
A novel kind of composite foaming agents for rigid PVC（R-PVC） was prepared from modifying azodicarbonamide（AC） with kickers（carbamide,zinc carbonate） and sodium bicarbonate.The samples were analyzed with thermal analysis and gas volume test.The results indicate that the novel composite foaming agent with a mass ratio of 10∶10∶2.5∶2.5,which represent AC,carbamide,zinc carbonate and sodium bicarbonate respectively,poses optimized properties： its decomposition temperature lies within the temperature range suitable for R-PVC processing,its endotherm equals exotherm on the whole and this composite foaming agent has a high volume of liberated gas but without any abruptness.R-PVC foam manufactured with this composite foaming agent has better mechanical properties,and its SEM images present fine microcellular structure.
参考文献
| [1] | Patterson J, .[J].Journal of Vinyl & Additive Technology,2001,7(03):138-141. |
| [2] | Diaz C A;Matuana L M .[J].Vinyl and Additive Tech- nology,2009,15(04):211-218. |
| [3] | Rabinovitch E B;Isner J D;Sidor J A et al.[J].Journal of Vinyl & Additive Technology,1997,3(03):210-215. |
| [4] | Mengeloglu F;Matuana L M .[J].Journal of Vinyl & Additive Technology,2003,9(01):26-31. |
| [5] | Marcilla A;Garcia-Quesada JC;Beltran MI;Ruiz-Femenia R .Study of the formulations and process conditions in the crosslinking of polyethylene foams at atmospheric pressure[J].Journal of Applied Polymer Science,2008(3):2028-2037. |
| [6] | Rapacki S R .[J].Journal of Vinyl & Additive Technology,1998,4(01):12-21. |
| [7] | Topol I A;Nemukhin A V;Dobrogorskaya Y I et al.[J].Journal of Physical Chemistry B,2001,105(45):11341-11350. |
| [8] | Reyes-Labarta JA;Marcilla A .Kinetic study of the decompositions involved in the thermal degradation of commercial azodicarbonamide[J].Journal of Applied Polymer Science,2008(1):339-346. |
| [9] | Schipper P S;Black J;Dymek T .[J].Vinyl and Addirive Technology,1996,2(04):304-309. |
| [10] | 黎继群,吴英瑜.ADC发泡剂发气量测定方法的改进[J].中国氯碱,2001(02):33-35. |
| [11] | Zoller, A.;Marcilla, A. .DSC study of foamable poly (vinyl chloride-co-vinyl acetate) plastisols of different commercial plasticizers[J].Journal of Applied Polymer Science,2011(6):3314-3321. |
| [12] | Reyes-Labarta JA;Olaya MM;Marcilla A .DSC study of transitions involved in thermal treatment of foamable mixtures of PE and EVA copolymer with azodicarbonamide[J].Journal of Applied Polymer Science,2006(3):2015-2025. |
| [13] | 周琼,于涛,郑鸿,吴其晔.典型放热型、吸热型和吸-放热型发泡剂热分解特性的研究[J].高分子材料科学与工程,2000(05):137-139. |
| [14] | 孔展,张卫勤,芦成,李国莉,李绍鹤,王长胜.PVC/木粉复合材料的发泡研究[J].塑料,2006(06):31-35. |
| [15] | Barzegari MR;Rodrigue D .The effect of density profile on the flexural properties of structural foams[J].Polymer engineering and science,2007(9):1459-1468. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%