采用反应烧结法制备了Mo2FeB2基金属陶瓷,用扫描电镜、能谱仪及X射线衍射仪等手段研究了烧结工艺和碳加入量对其显微组织和力学性能的影响.结果表明:随着碳加入量的增大,金属陶瓷的硬度和抗弯强度均先增大再减小;当添加0.5%的碳时,在1 100℃保温60 min并最终在1 280℃烧结60 min,能够获得完全致密且力学性能较好的MozFeB2基金属陶瓷,其抗弯强度达到1 176 MPa.
参考文献
| [1] | Takagi K. .High tough boride base cermets produced by reaction sintering[J].Materials Chemistry and Physics,2001(1/3):214-219. |
| [2] | Takagi K.;Komai M.;Yamasaki Y. .HIGH-STRENGTH BORIDE BASE HARD MATERIALS[J].International Journal of Quantum Chemistry,1997(1):243-248. |
| [3] | K. Nishiyama;M. Keino;Y. Furuyama .Internal friction of boride cermets at elevated temperatures[J].Journal of Alloys and Compounds: An Interdisciplinary Journal of Materials Science and Solid-state Chemistry and Physics,2003(1/2):97-102. |
| [4] | A. Saez;F. Arenas;E. Vidal .Microstructure development of WCoB-TiC based hard materials[J].International Journal of Refractory Metals & Hard Materials,2003(1/2):13-18. |
| [5] | 杨俊茹,刘福田,张悦刊,黄传真,李兆前.对金属陶瓷硬质覆层材料界面层扩散的研究[J].材料导报,2006(05):123-125. |
| [6] | 刘福田,李文虎,张英才,黄巍玲,杨俊茹,许坤,李兆前.硬质合金覆层-钢基体结合界面层及其生长模型的研究[J].陶瓷学报,2004(03):139-144. |
| [7] | 刘福田,李兆前,黄传真,常钧,芦令超,程新.三元硼化物基金属陶瓷覆层性能的研究[J].机械工程材料,2003(07):30-34. |
| [8] | 王永国,李兆前,张荻.新型金属陶瓷的耐腐蚀性能研究[J].机械工程材料,2003(10):25-27. |
| [9] | 卢伟民,张蓓,杨宣增,欧应龙.氧对Mo2FeB2金属陶瓷性能的影响[J].中国有色金属学报,1997(02):145-149. |
| [10] | 张梅琳,朱世根,朱守星.超细及纳米硬质合金中碳含量的变化及对组织性能的影响[J].材料导报,2006(08):65-68. |
| [11] | 王永国,李兆前,黄传真,武体真.钢用硬质覆层材料的显微结构分析[J].电子显微学报,2002(01):72-75. |
| [12] | 刘福田,李兆前,黄传真.三元硼化物基金属陶瓷复合材料及其液相烧结机理[J].济南大学学报(自然科学版),2001(04):291-295. |
| [13] | 刘福田,李兆前,黄传真,常钧,芦令超,程新.合金组分对金属陶瓷覆层材料性能影响的研究[J].硅酸盐通报,2003(02):38-42,61. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%