The structural change in heat affected zone(HAZ)and its influence on properties of welded white cast iron have been investigated by means of thermal cycle simulation technique.The structure of the white cast iron at peak temperature 800℃ was examined as cementite in pearlitic matrix,of which the hardness and impact toughness are the lowest,while the struc- ture after cyclic heating at high peak temperature is mainly cementite together with twin martensite,of which the hardness and impact toughness are rather higher.The phase bounda- ries in the structure of low hardness are smooth and regular as well as with fine precipitates. Both the cleavage and interphase fracture were revealed in the structure of low hardness,while the transgranular fracture was found in those areas of higher hardness.