采用不同改性剂对Mg(OH)2粒子进行改性，吸油值为考察指标，考察了不同改性剂对Mg(OH)2粒子的改性效果。研究了改性Mg(OH)2对PVC的阻燃性能和力学性能的影响。实验结果表明：改性剂为硬脂酸锌时，改性效果最佳，吸油值为33．39%，并对样品进行了红外和扫描电镜表征；随着改性Mg(OH)2的添加量不断增加，氧指数逐渐增大，但拉伸强度逐渐下降。当改性Mg(OH)2添加量为40份时，综合性能较好。
In this paper,Magnesium hydroxide was modified with different modifiers. And investigated the modi-fication effect of magnesium hydroxide by different modifiers. The influence of magnesium hydroxide on flame retar-dancy and mechanical properties of polyvinyl chloride were studied. The results showed that:zinc stearate was a better modifier,oil absorbed value was 33. 39%. The technique of infrared and scanning electron microscope was used to characterize the surface properties of product. With dosage of magnesium hydroxide was increasing,its oxy-gen index increased,but mechanical properties decreased gradually. It exhibited better comprehensive properties by adding 40 phr of modified magnesium hydroxide.
参考文献
| [1] | 赵建海,刘连生,赵连梅.纳米氢氧化镁表面改性研究[J].盐湖研究,2009(04):41-45. |
| [2] | 刘立华,宋云华,陈建铭,郭奋,陈建峰.纳米氢氧化镁表面改性研究[J].化工进展,2004(01):76-79. |
| [3] | 尹晓磊,袁建军.氢氧化镁阻燃剂的表面改性研究进展[J].天津化工,2008(05):8-10. |
| [4] | 董海波,杜志平,赵永红,周大鹏.改性纳米氢氧化镁的制备与表征[J].中国粉体技术,2010(06):67-70. |
| [5] | 丁孝初,岳林海,金达莱.有机质对氢氧化镁微晶结构的影响[J].浙江大学学报(理学版),2003(05):565-569. |
| [6] | 许端平 .阻燃用Mg(OH)2微胶囊技术[J].辽宁化工,2001,30(10):431-432,456. |
| [7] | 徐传辉,王万勋,陈玉坤,曾能,何慧,贾德民.氢氧化镁阻燃聚合物材料的研究进展[J].绝缘材料,2007(01):32-35. |
| [8] | 徐建中;尚俊敏 .疏水氢氧化镁的制备及其在阻燃PVC中的应用[D].河北:河北大学,2012. |
| [9] | 任拥军.改性氢氧化镁阻燃剂在阻燃PVC中的应用研究[J].河南化工,2007(07):31-32. |
| [10] | 王正洲,瞿保钧,范维澄,李治.表面处理剂在氢氧化镁阻燃聚乙烯体系中的应用[J].功能高分子学报,2001(01):45-48. |
| [11] | 张永兆,陈军.氢氧化镁表面有机化及在阻燃PVC中的应用[J].塑料工业,2010(z2):132-135,150. |
| [12] | 李辉 .纳米金属氧化物的制备及其在软PVC阻燃中的应用[D].合肥工业大学,2010. |
| [13] | 闫海妮,张正方,唐军.氢氧化镁的表面改性及其在PVC中的分散性研究[J].化学试剂,2011(01):62-64,68. |
| [14] | 刘立华.Mg（OH）2阻燃剂的表面改性及其在软质PVC中的应用[J].塑料科技,2010(02):89-93. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%