使用以Al粉、Cu粉混合,添加NaCl或无水K_2CO_3的混合配比,并采用燃烧反应合成的方法制备了规则的、具有良好吸声性能的开孔Al-Cu吸声材料.采用扫面电镜及X射线衍射对样品进行表征,并使用驻波管法测其吸声系数.实验结果表明:随着NaCl或无水K_2CO_3含量的增加, Al-Cu吸声材料的孔隙率及吸声系数随之增加;造孔剂为无水K_2CO_3的Al-Cu吸声材料,其吸声性能高于造孔剂为NaCl的;在反应过程中,没有Al、Cu单质残留,完全形成了Al-Cu金属间化合物.超声清洗后NaCl、无水K_2CO_3 均充分溶解.
By mixing powder Al and Cu adding NaCl or a mixture of anhydrous K_2CO_3 ratio,this study aims to produce a regular opening Al-Cu sound-absorbing material of good sound-absorbing properties by self-propagating high-temperature synthesis.The obtained materials were characterized by SEM,XRD.And absorption coefficient was tested with standing wave pipe method.The experimental results show: by adding NaCl or anhydrous K_2CO_3 into the Al-Cu based material and then after self-propagating high-temperature synthesis,with the content of NaCl and anhydrous K_2CO_3 increasing,the porosity increases,so does the absorption coefficient of the Al-Cu sound-absorbing material; the acoustic properties of the Al-Cu sound-absorbing material in which K_2CO_3 was taken as pore former are higher than those using NaCl as pore former;there are no residue of Al and Cu after the reaction,all turned into Al-Cu intermetallic compound.NaCl and anhydrous K_2CO_3 have been fully dissolved after ultrasonic cleaning.
参考文献
| [1] | 曾晓冬;李旭祥.[J].化工新型材料,1998(05):37-38. |
| [2] | 武小娟,孙伟成,隋志成.泡沫铝的制备与应用[J].新技术新工艺,2002(04):49-51. |
| [3] | YU Hai-jun,YAO Guang-chun,WANG Xiao-lin,LI Bing,YIN Yao,LIU Ke.Sound insulation property of Al-Si closed-cell aluminum foam bare board material[J].中国有色金属学会会刊(英文版),2007(01):93-98. |
| [4] | 苑改红,王宪成.吸声材料研究现状与展望[J].机械工程师,2006(06):17-19. |
| [5] | 姚广春;张晓明 .[P].中国:CN1320710,2001-11-7. |
| [6] | Andrews E W;Huang J S;Ggbson L J .[J].Acta Materialia,1999,47(10):2927-2935. |
| [7] | 李风,陈海燕,袁鸽成,叶永权.烧结多孔铝合金的孔隙参数分析[J].材料科学与工程,2002(02):254-258. |
| [8] | 王月.孔结构对通孔泡沫铝水声吸声性能的影响[J].材料开发与应用,2001(04):16-18. |
| [9] | 程和法 .[J].轻合金加工技术,2001,1(22):44-49. |
| [10] | 马广斌,朱正吼,夏小鸽.一种新型中低频吸声材料的研制[J].功能材料,2008(05):861-863. |
| [11] | Murotani T;Wang Zhou;Chen Wei-rong .[J].Materials Science Forum,2005,14(02):490-491. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%