为使高铝粉煤灰提氧化铝后产生的二次固废硅钙渣能够在水泥行业中被大量地消纳，以熟料中的f－CaO含量为指标，对不同配比硅钙渣水泥熟料的易烧性进行了研究，并采用XRD和ESEM对其进行分析。结果表明：硅钙渣能显著增加熟料烧成时的液相量，促进矿物晶体生成与长大，改善生料的易烧性；但当硅钙渣掺入量高于40％时，由于铝率的升高，使生料的易烧性下降。
To make a massive of silicate?calcium slag which is generated in process of extracting aluminum from high aluminum fly ash enable to be treated and utilized in the cement industry, the raw meal burn?ability for different content of silicate?calcium slag was researched by f-CaO content of clinker as the index, and the experimental results were analyzed by XRD and ESEM. The results indicated that the burn?ability of raw meal was markedly improved, because silicate?calcium slag was able to increase yield of liquid phase in the clinker and improve generation and grown of crystals. But when the content of silicate?calcium was more than 40%, the burn?ability of raw meal gradually decreased.
参考文献
| [1] | 孙俊民,王秉军,张占军.高铝粉煤灰资源化利用与循环经济[J].轻金属,2012(10):1-5. |
| [2] | 张战军 .从高铝粉煤灰中提取氧化铝等有用资源的研究[D].西北大学,2007. |
| [3] | 朱元基.硅钙渣作为水泥原料的研究[J].矿冶工程,1983(01):44. |
| [4] | 徐银芳 .硅钙渣作为水泥原料的研究[J].华中理工大学学报,1992,20(01):147-152. |
| [5] | 封培然.磷矿石尾矿配料的易烧性试验研究[J].水泥工程,2013(01):4-7. |
| [6] | Kamali A.;Mokhlisse A.;Benchanaa M. .The effect of chemical composition on the burnability of cement raw meal[J].Annales de Chimie-Science des Materiaux,1998(1/2):147-150. |
| [7] | CHEN Huxing,MA Xianwei,WANG Peiming.Effect of CuO on the Burnability and Mineral Formation of High C3S Cement Clinker[J].武汉理工大学学报（材料科学版）（英文版）,2010(05):838-844. |
| [8] | 温平.硅钙渣作为水泥生产原料的可行性研究[J].中国水泥,2012(05):54-55. |
| [9] | 杨志民.联合法赤泥用作活性水泥混合材[J].水泥,1992(04):18-23. |
| [10] | SINGH M;UPADHAYA S N .Preparation of special cements from red mud[J].WASTE MANAGEMENT,1996,16(08):665-670. |
| [11] | 李秋生.铝工业废渣利用与开发[J].轻金属,1995(01):26-28. |
| [12] | 刘子高,杨昌适,程宗浩,艾际井.拜耳法赤泥的处理和利用[J].中国有色金属学报,1997(01):40-44. |
| [13] | 房永广 .高碱赤泥资源化研究及其应用[D].武汉理工大学,2010. |
| [14] | 张乐观,王国贞,段璐淳.水洗处理赤泥初步脱碱[J].无机盐工业,2011(02):57-58. |
| [15] | 李耀刚,王雅琼,王克勤,闫子春.烧结法赤泥脱碱过程[J].化工冶金,1998(04):309-312. |
| [16] | CLARK B A;BROWN P W .The formation of calcium sulfoaluminate hydrate compounds:part Ⅱ[J].Cement and Concrete Research,2000,30(02):233-240. |
| [17] | 任根宽.用改性赤泥为原料制备水泥[J].化工环保,2008(06):526-530. |
| [18] | P.E. Tsakiridis;S. Agatzini-Leonardou;P. Oustadakis .Red mud addition in the raw meal for the production of Portland cement clinker[J].Journal of hazardous materials,2004(1/2):103-110. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%