Paint baking treatment was carried out in a silicon oil bath at 170℃ for 20min for Si-Al-Mn TRIP Steel sheet with different prestrains, and effect of prestrain on microstructures and properties was studied before and after baking. The results show that with the increasing of prestrain amount during prestraining and baking, the volume fraction of retained austenite decreases, and the volume fraction of martensite and bainite increases as well as yield strength increases; as prestrain ranges from 0 to 4%, the baking-hardening (BH) value increases; while the prestrain ranges from 4% to 16% , the BH value decreases; when the prestrain amount is 4% , the highest BH value is about 70 Mpa for Si-Al-Mn TRIP steel sheet with niobium, which displays excellent baking-hardening behavior.
参考文献
| [1] | Ushilda K .Rencent Developments in Steel Sheets[J].Scandinavian Journal of Metallurgy,1999,28:33. |
| [2] | Hiroshi M;Fusato K;Kohei H .Metallurgy of Continuously Annealed High Strength TRJP Steel Sheet[J].Steel Research International,2002,73(06):211. |
| [3] | Srivastava A K;Bhattacharjee D;Jhab G .Microstructural and Mechanical Characterization of C-Mn-Al-Si Cold-Rolled TRIP-Aided Steel[J].Materials Science and Engineering,2007,A445-446:549. |
| [4] | TANG Zheng-you;DING Hua;DU Lin-xiu et al.Study on Microstructures and Mechanical Properties of Si-Al-Mn TRIP Steel With Niobium[J].Journal of Materials Science and Technology,2007,23(06):790. |
| [5] | Manabu T .Metallurgical Aspect of Sheet Steels for Automobiles[J].Materials Science and Technology,2004,74(05):459. |
| [6] | Sakata K;Matsuoka S;Sato K.Highly Formable Sheet Steel for Automobile Through Advanced Microstructure Control Technology[J].Kawasaki Steel Technical Report,2003(48):37. |
| [7] | A. Rusinek;J.R. Klepaczko .Experiments On Heat Generated During Plastic Deformation And Stored Energy For Trip Steels[J].Materials & design,2009(1):35-48. |
| [8] | Lee C G;Kim S J;Song B H et al.Effect of Heat Treatment on Formability in 0.15C-1.5Si-l.5Mn Multiphase Cold-Rolled Steel Sheet[J].Metals and Meterials International,2002,8(05):435. |
| [9] | Lin LI,B.C.De Cooman,P.Wollants,Yanlin HE,Xiaodong ZHOU.Effect of Aluminum and Silicon on Transformation Induced Plasticity of the TRIP Steel[J].材料科学技术学报(英文版),2004(02):135-138. |
| [10] | Kaneko S;Matsuoka S;Sakata K .Strengthening Mechanism in Hot-Rolled High Strength Sheet With Increase in Tensile Strength Induced by Bake Hardening[J].Journal of the Iron & Steel Institute of Japan,2003,89(10):1057. |
| [11] | Kaneko S;Hiramoto J;Ishikawa T.Development of Hot-Rolled Sheet Steel With Significantly Increased Tensile Strength Induced by Strain Age Hardening[J].Kawasaki Steel Technical Report,2003(35):28. |
| [12] | Bleck W;Frehn A;Kechagias E et al.Control of Micro-structure in TRIP Steels by Niobium[J].Materials Science Forum,2003,426-432:43. |
| [13] | Yu CHEN,Guoyi TANG,Haoyang TIAN,Feipeng LI,Yu ZHANG,Lihui WANG,Zhaojun DENG,Dexing LUO.Microstructures and Mechanical Properties of Nb-Ti Bearing Hot-rolled TRIP Steels[J].材料科学技术学报（英文版）,2006(06):759-762. |
| [14] | Girault E;Jacques P;Harlet P .Metallographic Methods for Revealing the Multiphase Microstructure of TRIP-Assisted Steels[J].Materials Characterization,1998,40(02):111. |
| [15] | Furnemont Q.;Kempf M.;Jacques PJ.;Goken M.;Delannay F. .On the measurement of the nanohardness of the constitutive phases of TRIP-assisted multiphase steels[J].Materials Science & Engineering, A. Structural Materials: Properties, Misrostructure and Processing,2002(1/2):26-32. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%