在VLDPE/Mg(OH)2(100/160,质量比)体系中加入具有不同玻璃化温度的两种聚丙烯酸酯包覆剂,用扫描电子显微镜观察以四氢呋喃刻蚀前后的试样,证实了包覆剂分布在填料颗粒与PE的界面.动态力学研究表明,填料使PE的储存模量和损耗模量上升,而加入高分子包覆剂后,当温度低于包覆剂的玻璃化温度时使储存模量略有增加,而在温度高于其玻璃化温度时使储存模量下降.
参考文献
| [1] | Nielsen L E .[J].Journal of Applied Polymer Science,1966,24:649. |
| [2] | Danusso F;Tieghi G .[J].Polymer,1986,27:1385. |
| [3] | Kolarik J;Jancar J .[J].POLYMER,1992,33:4961. |
| [4] | Scott C;Ishida H;Maurer F H J .[J].Journal of Materials Science,1987,22:3963. |
| [5] | Enikolopyan N S;Fridman M L;Stalnova I O et al.[J].Advances in Polymer Science,1990,96:1. |
| [6] | Chanliau-Blanot M T;Nardin M;Donnet J B et al.[J].Journal of Materials Science,1989,24:641. |
| [7] | Chanliau-Blanot M T;Nardin M;Donnet J B et al.[J].Journal of Materials Science,1989,24:649. |
| [8] | Manson J A;Sperling L H.Polymer Blends and Composites[J].Platinum Metals Review,1976 |
| [9] | Christensen R M.Mechanics of Composite Materials[M].Wiley-Interscience,New York,1979 |
| [10] | Chacko V P;Karasz F E;Farris R J .[J].Polymer Engineering and Science,1982,22(15):968. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%