采用乳液聚合技术将丙烯酸丁酯(BA)和丁二烯(Bd)、苯乙烯(St)共聚制备P(BA-co-Bd-co-St)胶乳(简称丁苯酯),然后在丁苯酯乳胶粒子上接枝St和AN合成P(BA-co-Bd-co-St)-g-SAN接枝共聚物.将其与SAN树脂熔融共混制备P(BA-co-Bd-co-St)-g-SAN/SAN共混物,研究了丁苯酯胶乳的粒径和组成对共混物力学性能和形态结构的影响.结果发现,引入丁二烯大大提高了SAN共聚物的接枝率,改善了共混物的冲击韧性,随着丁苯酯胶乳粒径的增加,共混物的冲击强度呈现先增大后减小的趋势.形态研究表明,丁二烯的引入显著改善了橡胶粒子在SAN树脂中的分散状况,但当粒径较小时,橡胶粒子发生了聚集.
参考文献
| [1] | 沈勇,王炼石,张安强.PBA-g-SAN的表征及其对SAN树脂的增韧作用[J].弹性体,2007(02):37-41. |
| [2] | Bouvier-Fontes L;Pirri R;Asua JM;Leiza JR .Cross-linking emulsion copolymerization of butyl acrylate with diallyl maleate[J].Journal of Polymer Science, Part A. Polymer Chemistry,2005(20):4684-4694. |
| [3] | SINGA TOBING;ANDREW KLEIN;L.H.SPERLING;BOB PETRASKO .Effect of Network Morphology on Adhesive Performance in Emulsion Blends of Acrylic Pressure Sensitive Adhesives[J].Journal of Applied Polymer Science,2001(9):2109-2117. |
| [4] | 耿丽丽,任亮,韩业,张明耀,张会轩.PBA-g-SAN对ASA树脂结构与性能的影响[J].中国塑料,2011(03):29-33. |
| [5] | Tolue, S;Moghbeli, MR;Ghafelebashi, SM .Preparation of ASA (acrylonitrile-styrene-acrylate) structural latexes via seeded emulsion polymerization[J].European Polymer Journal,2009(3):714-720. |
| [6] | 赵海燕,王江涛,赵惠珠,解金鹏,张立群,瞿雄伟.AAS核壳结构共聚物的制备及其改性SAN树脂的性能[J].高分子材料科学与工程,2011(01):9-11,16. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%