研究了热处理对Ti49.8Ni50.2合金丝材的相变、力学性能以及热机械循环疲劳的影响.结果表明:随着退火温度的升高,R→B19'相变温度升高,B2→R相变温度降低,873 K退火时B2→R和R→B19'相变重合.当退火温度(Ta)低于823 K时,试样处于回复阶段,σM随退火温度升高有小幅度下降,723 K退火试样在热机械循环中获得最大稳定回复应变, 疲劳寿命随退火温度的升高略有提高;退火温度高于823 K时,试样发生再结晶,σM剧烈下降,稳定回复应变剧烈降低,而疲劳寿命由103升至104数量级.
参考文献
| [1] | 赵连城,郑玉峰.形状记忆与超弹性镍钛合金的发展和应用[J].中国有色金属学报,2004(z1):323-326. |
| [2] | 杨冠军,邓炬.Ti-Ni-Nb宽滞后记忆合金的研究进展[J].稀有金属材料与工程,1998(06):322. |
| [3] | Conard J M;Mills J W.Stiquito for Beginners-An Introduction to Robotics[M].Wiley-Interscience:IEEE Computer Society,1999:7. |
| [4] | Hashimoto M.[J].Journal of Robotic Systems,1985(01):3025. |
| [5] | Ikuta K.[J].IEEE Transactions on Robotics and Automation,1990(03):2151. |
| [6] | Hwang C M;Meichle M;Salamon M B et al.[J].Philosophical Magazine A:Physics of Condensed Matter:Structure Defects and Mechanical Properties,1983,47:31. |
| [7] | 贺志荣,王芳,周敬恩.Ni含量和热处理对Ti-Ni形状记忆合金相变和形变行为的影响[J].金属热处理,2006(09):17-21. |
| [8] | Fukuda T;Saburi T;Dio K et al.[J].Materials Transactions,1992,33:271. |
| [9] | Saikrishna C N;Ramaiah Venkata K et al.[J].Materials Science and Engineering A:Structural Materials Properties Microstructure and Processing,2006,428:217. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%