The density, microstructure and magnetic properties of non-doped Mn-Zn ferrite nanoparticles sintered compacts were investigated. The compacts of non-doped Mn-Zn ferrite nanoparticles were sintered by segmented-sintering process at lower sintering temperature. The density of sintered samples was measured by Archimedes method, and the phase composition and microstructure were examined by XRD and SEM. The sintered Mn-Zn ferrite magnetic measurements were carried out with Vibrating Sample. The results show that the density of sintered compacts increases with the rising of sintering temperature, achieving 4.8245 g·cm-3 when sintered at 900 ℃, which is the optimal density of Mn-Zn functional ferrite needed and from the fractured surface of sintered samples, it can be seen that the grain grows well with small grain size and homogeneous distribution.
参考文献
| [1] | Tsay C Y;Liu K S;Lin I Nan .Co-firing procress using conventional and microwave sintering technologies for Mn-Zn and Ni-Znferrites[J].Euro Ceram Soc,2001,21:1937. |
| [2] | Ken H;Tatsuji A;Sinsuke E et al.Microstructures and magnetic and electric properties of low-temperature sintering Mn-Zn ferrites without and with addition of lithium borosilicate glass[J].Magnetism and Magnetic Materials,1999,205:283. |
| [3] | Ott G;Wrba J;Lucke R .Recnet developments of Mn-Zn ferrites for high permeability applications[J].Magnetism and Magnetic Materials,2003,254-255:535. |
| [4] | Hague DC.;Mayo MJ. .SINTER-FORGING OF NANOCRYSTALLINE ZIRCONIA .1. EXPERIMENTAL[J].Journal of the American Ceramic Society,1997(1):149-156. |
| [5] | Allen AJ.;Skandan G.;Long GG.;Hahn H.;Kerch HM.;Parker JC.;Ali MN.;Krueger S. .MICROSTRUCTURAL EVOLUTION DURING THE SINTERING OF NANOSTRUCTURED CERAMIC OXIDES[J].Journal of the American Ceramic Society,1996(5):1201-1212. |
| [6] | Chen PL.;Chen IW. .SINTERING OF FINE OXIDE POWDERS .2. SINTERING MECHANISMS[J].Journal of the American Ceramic Society,1997(3):637-645. |
| [7] | Mishra R S;Lesher C E;Mukherjee A K .High-Pressure Sintering of Nanocrystalline γ-Al2O3[J].Journal of the American Chemical Society,1996,79:2989. |
| [8] | Viadimir V S;Markus W;Horst H .Sintering behavior of nanocrystalline zirconia doped with alumina prepared by chemical vapor synthesis[J].Journal of The American Chemical Society,2003,83(08):1853. |
| [9] | Yu T;Jingfeng L.New Materials Conspectus[M].北京:冶金工业出版社,2004 |
| [10] | 崔银芳,王新,魏雨,郝顺利,王永明.软磁锰锌铁氧体纳米晶的制备及测试分析[J].人工晶体学报,2005(06):1096-1099. |