高炉采用3级除尘后，其第2级的旋风灰中含有大量的含铁氧化物和碳，将其作为喷吹煤粉的添加剂从高炉风口喷入，可促进煤粉燃烧，达到高效利用旋风灰的目的。对首秦高炉除尘灰进行粒度和化学成分分析，发现旋风灰可以作为添加剂与煤粉进行混合喷吹。通过实验室测定不同含量旋风灰对煤粉燃烧性的影响，确定在富氧率为3%，添加旋风灰比例为6%时，可达到最佳的煤粉燃烧效果。首秦高炉的试验结果表明，喷煤时添加3%以下的旋风灰代替相应的煤粉，生产平稳，喷吹系统运转正常。高炉自产的旋风灰作为煤粉添加剂是可行的，可以带来较好的经济效益和社会效益。
The cyclone dust of the second stage contains plenty of oxides-containing iron and carbon. Thus, it can be an efficient utilization to inject the cyclone dust back into the furnace as the additive, which can improve the combustion rate of the pulverized coal. The size distribution and chemical compositions of the dedusting ash of Shouqin BF was analyzed, which demonstrated the feasibility of adding cyclone dust as the additive of pulverized coal. Afterwards, the effects of adding different proportions of cyclone dust on the combustion of pulverized coal were determined. The optimum combustion results can be reached when the oxygen enrichment is 3% and the proportion of added cyclone dust is 6%. The experimental results of BF at Shouqin Company shows that the PCI system runs well and the production is stable when the proportion of added cyclone dust is below 3%. Therefore, adding the BF cyclone dust as the additive of pulverized coal is feasible, which will bring good economic and social benefits.
参考文献
| [1] | |
| [2] | 彭其春，周飞，郭宜彬．高炉用煤粉的混合添加剂研究[J]．钢铁钒钛，2008,29(3)：22-24.Peng Qichun，Zhou Fei，Guo Yibin. Study on Pulverized Coal with Mixture AdditiveUsed for Blast Furnace in Laboratory[J]. IRON STEEL VANADIUM TITANIUM，2008,29(3)：22-24.[2] 寇建兵, 罗果萍, 张芳.包钢高炉除尘灰中有害元素分析研究[J].中国冶金,2011,21(3)：44-46. KOU Jianbing , LUO Guoping, ZHANG Fang. Research on Harmful Elements in the Dust Eliminated From Blast Furnace Gas of Baogang[J]. China Metallurgy,2011,21(3)：44-46.[3] 张海滨，吴铿，周翔，等.煤粉特性及配煤的研究[J].中国冶金，2008,18(8)：1-3.ZHANG Haibin,WU Keng,ZHOU Xiang, et al. Research of Coal Properties and Blending. China Metallurgy.2008,18(8)：1-3.[4] 张二华，吴铿，万鹏，等. SiO2还原对高炉风口前理论燃烧温度的影响[J].北京科技大学学报，2010，36,：1024-1027.ZHANG Erhua, Wu Keng, Wan Peng, et al. The Effect of the Reduced SiO2 on the Theoretical Flame Temperature before Tuyere in BF[J]. JOURNAL OF UNIVERSITY OF SCIENCE AND TECHNOLOGY BEI JING, 2010,36: 1024-1027.[5] 那树人. 炼铁工业计算[M]. 北京：冶金工业出版社，2005，276-287.Na S R puddling Calculation Beijing: Metallurgical Industry Press. 2005, 276-287 |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%