采用固相反应合成了LiMnO2和LiMn0.9Cr0.1O2,Cr的加入改变了LiMnO2的结构,与LiMnO2 正交结构(空间群 Pmnm)相比,LiMn0.9Cr0.1O2具有单斜结构(空间群 C2/m).充放电过程中,LiMnO2和LiMn0.9Cr0.1O2结构产生向尖晶石结构的不可逆转变.在首次放电过程中,LiMnO2只存在2.9 V的电压平台,随着循环次数的增加,在2.9 V和4 V电压平台容量都有所增加.与LiMnO2不同,LiMn0.9Cr0.1O2在首次放电过程中存在有2.9 V和4 V电压平台,随着循环次数的增加,4 V电压平台容量逐渐减小,在一定循环次数下,只有2.9 V的电压平台存在.因此,Cr的掺杂不仅改变了LiMnO2的结构,而且改变其电化学行为.
LiMnO2 and LiMn0.9Cr0.1O2 were prepared by a high temperature solid-state route. In comparison with orthorhombic LiMnO2, monoclinic LiMnO2 was formed with Cr substitution. The research shows that the irreversible transformation to spinel-like structure during LiMnO2 cycling is a gradual phase transformation process. In comparison with the 2.9 V and 4 V plateaus of LiMnO2, LiMn0.9Cr0.1O2 shows only 2.9 V plateau for further cycling. So it is clear that the electrochemistry behavior change from LiMnO2 to LiMn0.9Cr0.1O2 phase is due to doping of Cr.
参考文献
| [1] | Hoppe R;Brachtel G;Jansen M;Armstrong A R, Bruce P G. Davidson I J, McMillan R S, Slegr H et al. Armstrong A R, Bruce P G. Davidson I J, McMillan R S, Slegr H et al.Electrochemistry And Structure of Li2-xCryMn2-yO4 Phases[J].Journal of Power Sources,1999,81-82(06):406-411. |
| [2] | GUMMOW R J;Thackeray M M .An Investigation of Spinel- Related and Orthorhombic LiMnO2 Cathodes for Rechar- geable Lithium Batteries[J].Journal of the Electrochemical Society,1994,141(05):1178-1182. |
| [3] | Kotschau I M;Dahn J R .In Situ X-Ray Study of LiMnO2[J].Journal of the Electrochemical Society,1998,145(08):2672-2677. |
| [4] | THACKERAY M M;David W I F;Bruce P G et al.Lithium Insertion Into Manganese Spinels[J].Materials Research Bulletin,1983,18(04):461-472. |
| [5] | Vitins G.;West K. .LITHIUM INTERCALATION INTO LAYERED LIMNO2[J].Journal of the Electrochemical Society,1997(8):2587-2592. |
| [6] | Shao-Horn Y;Hackney S A;Armstrong A R et al.Structural Characterization of Layered LiMnO2 Electrodes by Electron Diffraction and Lattice Imaging[J].Journal of the Electrochemical Society,1999,146(07):2404-2412. |
| [7] | Bruce Peter G;Armstrong A R;Gitzendanner Robert .New Interaction Compounds for Lithium Batteries Layered LiMnO2[J].Journal of Materials Chemistry,1999,9(01):193-198. |
| [8] | Y.Chiang;D.R.Sadoway .High Capacity, Temperature-Stable Lithium Aluminum Manganese Oxide Cathodes for Rechargeable Batteries[J].Electrochemical and solid-state letters,1999(3):107-110. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%