采用CO2激光诱导Fe(CO)5-C2H4-NH3的气相分解反应制备了Fe、Fe-N和Fe-C-N超细微粒(微粒直径小于100 nm),用透射电子显微镜、X光衍射、O/N和C/S测试仪及振动样品磁强计等研究了微粒的结构、表面形态、表面氧的状态及磁性能等;探讨了碳对微粒的氧化特征,特别是对微粒表面氧的形态及其磁性能的影响.结果表明,微粒表面氧的状态可分为吸附态和化合态,并且二者的含量随着微粒的种类不同而变化,碳对微粒表面氧的存在状态、微粒的氧化状况及磁性能具有决定性的影响.
参考文献
| [1] | Suziki S;Sakumoto H;Miya S et al.[J].IEEE Transactions on Magnetics,1984,20(01):39. |
| [2] | Chubachi R;Tamayawa N .[J].IEEE Transactions on Magnetics,1984,20(01):45. |
| [3] | Sharrock M P.[J].MRS Bulletin,1990(53) |
| [4] | Tagawa K;Kita E;Tasaki A .[J].Japanese Journal of Applied Physics,1982,21(03):1596. |
| [5] | Gangopadhyay S;Hadjipanayis G C;Dale B et al.[J].Physical Review B,1992,45(17):9778. |
| [6] | Tasaki A;Saegusa N;Oda M .[J].IEEE Transactions on Magnetics,1983,19(05):1731. |
| [7] | Tasaki A;Tagawa K;Kita E et al.[J].IEEE Transactions on Magnetics,1981,17(08):3026. |
| [8] | Saegusa N;Tsukagoshi T;Kita E et al.[J].IEEE Transactions on Magnetics,1983,19(05):1629. |
| [9] | Bao X;Metzger R M;Doyle W D .[J].Journal of Applied Physics,1993,73(10):6734. |
| [10] | Zhao X Q;Liang Y;Zheng F et al.[J].Materials Letters,1994,21(11):285. |
| [11] | Hofer L;Cohn E M .[J].Journal of the American Chemical Society,1959,81(02):1176. |
| [12] | Tajima S;Hirano S .[J].Japanese Journal of Applied Physics,1990,29(04):662. |
| [13] | Hirano S;Tajima S .[J].Journal of Materials Science,1990,25(12):4457. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%