对Fe-26Mn-6Si-7Cr-1Cu和Fe-20Mn-6Si-7Cr-1Cu两种Fe基形状记忆合金进行了超声波振动空蚀试验,结果表明,两种合金都具有优良的抗空蚀性能,比较而言,Fe-26Mn-6Si-7Cr-1Cu合金的抗空蚀性能优于Fe-20Mn-6Si-7Cr-1Cu合金.在局部载荷作用下可吸收较多弹性变形能及在空蚀过程中有较高应变诱发马氏体相变能是前者抗空蚀性能优于后者的主要原因.
参考文献
| [1] | 李诗卓;董祥林.材料的冲蚀磨与微动磨损[M].北京:机械工业出版社,1987 |
| [2] | Li D Y .[J].WEAR,1998,221(02):116-123. |
| [3] | Liang Y N;Li S Z;Jin Y B et al.[J].Wear,1996,198(1-2):236-241. |
| [4] | Richman R H;Rao A S;Kung D .[J].Wear,1995,181-183(01):80-85. |
| [5] | Richman R H;Hodgson D E;Rao A S .[J].Wear,1992,157(02):401-407. |
| [6] | Wu S K;Lin H C;Yeh C H .[J].Wear,2000,244(1-2):85-93. |
| [7] | 龙霓东,王再友,朱金华.低层错能FeMnSiCrCu形状记忆合金的空蚀[J].机械工程材料,2003(04):7-9,13. |
| [8] | Olson G B;Cohen M .[J].Metallurgical and Materials Transactions,1976,7A(12):1897-1904. |
| [9] | Olson G B;Cohen M .[J].Metallurgical and Materials Transactions A:Physical Metallurgy and Materials Science,1976,7A(12):1915-1923. |
| [10] | 李成劳 .Behavior of γ<=>ε Martensite Transfo- rmation and Shape Memory Effect in Low Stacking Fault Energy Fe-Mn-Si-Cr-Ni System Alloys[D].Xi'an:Xi'an Jiaotong University,1998. |
| [11] | Cheng F T;Shi P;Man H C .[J].Scripta Materialia,2001,45(09):1083-1089. |
| [12] | Liu R;Li D Y .[J].材料科学与工艺(英文版),2000,16(03):328-332. |
| [13] | 龙霓东,朱金华.Ti3Al基合金的弹性变形能与空蚀[J].中国有色金属学报,2003(03):560-564. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%