The Compressive strength, porosity and pore size distribution of high performance metakaolin (MK) concrete were investigated. Concretes containing 0,5%,10% and 20% metakaolin were prepared at a water/cementitious material ratio (W/C) of 0.30. In parallel, concrete mixtures with the replacement of cement by 20% fly ash or 5 and 10% silica fume were prepared for comparison. The specimens were cured in water at 27℃ for 3 to 90 days. The results show that at the early age of curing (3 days and 7 days), metakaolin replacements increase the compressive strength, but silica fume replacement slightly reduces the compressive strength. At the age of and after 28 days, the compressive strength of the concrete with metakaolin and silica fume replacement increases.A strong reduction in the total porosity and average pore diameter were observed in the concrete with MK 20% and 10% in the first 7 days.
参考文献
| [1] | F Massazza;G Oberti.Durability of Pozzolanic Cements and Italian Experience in Mass Concrete[A].American Concrete Institute,Montreal,Canada,1991:1259-1283. |
| [2] | O Gjorv.High strength concrete[A].American Concrete Institute,Montreal,Canada,1992:21-77. |
| [3] | Bredy P;Chabannet M;Pera J .Microstructure and Porosity of Metakaolin Blended Cements[J].Materials Research Society Symposium Proceedings,1989,137:431-436. |
| [4] | De Silva P S;Glasser F P .Pozzolanic Activation of Metakaolin[J].Advances in Cement Researh,1992,4(04):167-178. |
| [5] | FELDMAN R F;Huang Cheng-yi .Properties of Portland Cement-silica Fume Pastes I.Porosity and Surface Properties[J].Cement and Concrete Research,1985,15(05):765-774. |
| [6] | Ambroise J;Murat M;Pera J .Hydration Reaction and Hardening of Calcined Clays and Related Minerals. V. Extension of the Research and General Conclusion[J].Cement and Concrete Research,1985,15(02):261-268. |
| [7] | Murat M .Hydration Reaction and Hardening of Calcined Clays and Related Minerals.I.Preliminary Investigation on Metakaolinite[J].Cement and Concrete Research,1983,13(02):259-266. |
| [8] | Ambroise J;Maximilien S;Pera J .Properties of Metakaolin Blended Cements[J].Adv Cem Mat(US),1994,1(01):161-168. |
| [9] | Kostuch J A;Walters G V;Jones T R.High Performance Concretes Incorporating Metakaolin-a Review[A].,1993:1799-1811. |
| [10] | Caldarone M K;Gruber K A;Burg R G .High-reactivity Metakaolin:A New Generation Mineral Admixture[J].Concrete International,1994,16(11):37-40. |
| [11] | B.B. Sabir;S. Wild;J. Bai .Metakaolin and calcined clays as pozzolans for concrete: a review[J].Cement & concrete composites,2001(6):441-454. |
| [12] | Khatib J M;Wild S .Pore Size Distribution of Metakaolin Pastes[J].Cement and Concrete Research,1996,26(10):1545-1553. |
| [13] | M Frises;J Cabrera .Pore Size Distribution and Degree of Hydration of Metakaolin-Cement Pastes[J].Cement and Concrete Research,2001,30:561-569. |
| [14] | L Day;B K Marsh .Measurement of Porosity in Blended Cement Pastes[J].Cement and Concrete Research,1988,18:63-73. |
| [15] | H F W Taylor.Cement Chemistry[M].London:Academic Press,1990 |
| [16] | M H Zhang;V M Malhotra .Characteristics of a Thermally Activated Alumino-silicate Pozzolanic Material and Its Use in Concrete[J].Cement and Concrete Research,1995,25(08):1713-1725. |
- 下载量()
- 访问量()
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%