目的 研究IMR纳米复合涂层对飞机外部结构件的防护性能.方法 对比考察典型加速腐蚀环境条件下,飞机外部结构模拟件表面聚氨酯面漆涂层和IMR21纳米复合涂层的腐蚀失效行为.结果 在经过2个阶段各8个周期的加速腐蚀后,模拟件涂层表面均出现了鼓包、开裂、剥落等现象,而且涂层在第二阶段的腐蚀程度略重于第一阶段.与聚氨酯面漆涂层相比,IMR21纳米复合涂层的腐蚀失效程度要低很多,说明该纳米复合涂层具有优良的抗环境腐蚀性能.结论 可考虑在飞机结构制造、大修以及外场维护中采用IMR21纳米复合涂层进行表面防腐涂装处理.
参考文献
| [1] | 舒畅,刘彬,周漪.锌铝/富铝复合涂层在海洋环境中的耐蚀性研究[J].表面技术,2012(05):56-59. |
| [2] | 陈群志,房振乾,康献海.军用飞机外场腐蚀防护方法研究[J].装备环境工程,2011(02):72-77. |
| [3] | NIKOLAOS D A;CHARIS J D;PANAGIOTIS S et al.Accelerated Corrosion Exposure in Ultra Thin Sheets of 2024 Aircraft Aluminum Alloy for GLARE Applications[J].Corrosion Science,2012,55:289-300. |
| [4] | 曹宏涛,李雪亭.基于海洋环境的紧固件腐蚀防护要求及技术措施[J].表面技术,2013(01):105-108. |
| [5] | 李晨钰,朱立群,刘慧丛,叶序斌,刘建中,黄颐.温度对2A12铝合金在模拟油箱积水环境中初期腐蚀行为的影响[J].航空学报,2013(06):1493-1500. |
| [6] | C.F. Dong;H. Sheng;Y.H. An;X.G. Li;K. Xiao;Y.F. Cheng .Corrosion of 7A04 aluminum alloy under defected epoxy coating studied by localized electrochemical impedance spectroscopy[J].Progress in Organic Coatings: An International Review Journal,2010(3):269-273. |
| [7] | JELENA B B;INGRID M;(Z)ELJKA J et al.Studies on Adhesion Characteristics and Corrosion Behaviour of Vinyltriethoxysilane/Epoxy Coating Protective System on Aluminum[J].Applied Surface Science,2010,256:3508-3517. |
| [8] | 李旭东,朱武峰,穆志韬,刘治国.LD2铝合金腐蚀行为研究[J].装备环境工程,2013(01):8-12,25. |
| [9] | Markevicius, G.;Chaudhuri, S.;Bajracharya, C.;Rastogi, R.;Xiao, J.;Burnett, C.;Chastek, T.Q. .Polyoligomeric silsesquioxane (POSS)-hydrogenated polybutadiene polyurethane coatings for corrosion inhibition of AA2024[J].Progress in Organic Coatings: An International Review Journal,2012(4):319-327. |
| [10] | 罗来正,肖勇,陈智君,王通洲,舒畅.航空用2D12铝合金在海洋大气环境中的腐蚀行为研究[J].装备环境工程,2012(04):39-41,51. |
| [11] | Microstructure and pitting corrosion of friction stir welded joints in 2219-O aluminum alloy thick plate[J].Corrosion Science: The Journal on Environmental Degradation of Materials and its Control,2009(11):2743. |
| [12] | 李郑琦,何宇廷,邵青,魏鹏.基于支持向量机的机载产品延长日历寿命方法[J].空军工程大学学报（自然科学版）,2010(04):6-10. |
| [13] | DENNIS E T;KIRILL L L;CHAVANIN S et al.Nanocomposite of Polypyrrole and Alumina Nanoparticles as a Coating Filler for the Corrosion Protection of Aluminum Alloy 2024-T3[J].Applied Surface Science,2008,254:5452-5459. |
| [14] | DAN Z H;TAKIGAWA S;MUTO I et al.Applicability of Constant Dew Point Corrosion Tests for Evaluating Atmospheric Corrosion of Aluminum Alloys[J].Corrosion Science,2011,53:2006-2014. |
| [15] | 陈群志,韩恩厚,李祥海,刘福春,张蕾.IMR纳米复合涂层与现役飞机典型涂层抗紫外线老化性能对比研究[J].腐蚀科学与防护技术,2005(04):234-236. |
| [16] | 穆志韬,陈定海,朱做涛,丁文勇,田述栋.腐蚀条件下LD2航空铝合金裂纹扩展规律研究[J].航空学报,2013(03):574-579. |
| [17] | 陈群志,房振乾.飞机结构日历寿命及腐蚀防护研究应关注的问题[J].装备环境工程,2012(06):72-77. |
上一张
下一张
上一张
下一张
计量
- 下载量()
- 访问量()
文章评分
- 您的评分：
-
10%
-
20%
-
30%
-
40%
-
50%